Abstract:Oxygen activation is a key step in the catalytic oxidation of formaldehyde (HCHO) at room temperature. In this study, we synthesized a carbon/Co3O4 nanocomposite (C-Co3O4) as a solution to the insufficient capability of pristine Co3O4 (P-Co3O4) to activate oxygen for the first time. Oxygen activation was improved via carbon preventing the agglomeration of Co3O4 nanoparticles, resulting in small particles (approximately 7.7 nm) and more exposed active sites (oxygen vacancies and Co3+). The removal efficiency of C-Co3O4 for 1 ppm of HCHO remained above 90%, whereas P-Co3O4 was rapidly deactivated. In static tests, the CO2 selectivity of C-Co3O4 was close to 100%, far exceeding that of P-Co3O4 (42%). Various microscopic analyses indicated the formation and interaction of a composite structure between the C and Co3O4 interface. The carbon composite caused a disorder on the surface lattice of Co3O4, constructing more oxygen vacancies than P-Co3O4. Consequently, the surface reducibility of C-Co3O4 was improved, as was its ability to continuously activate oxygen and H2O into reactive oxygen species (ROS). We speculate that accelerated production of ROS helped rapidly degrade intermediates such as dioxymethylene, formate, and carbonate into CO2. In contrast, carbonate accumulation on P-Co3O4 surfaces containing less ROS may have caused P-Co3O4 inactivation. Compared with noble nanoparticles, this study provides a transition metal-based nanocomposite for HCHO oxidation with high efficiency, high selectivity, and low cost, which is meaningful for indoor air purification.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.1c00490?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.1c00490</a>.Additional detail information including catalyst characterizations, low-concentration HCHO removal efficiency in different relative humidities, Co K-edge k3χ spectra, TG curves, N2 adsorption–desorption isotherms, SEM, TEM images and, EDS mapping, CV curves, and changes of surface OH and H2O peak intensity during in situ DRIFTS studies (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.1c00490/suppl_file/es1c00490_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Formaldehyde Oxidation over Co@N-Doped Carbon at Room Temperature: Tunable Co Size and Intensified Surface Electron Density

Cobalt Nanoparticles Encapsulated in Porous Nitrogen-Doped Carbon: Oxygen Activation and Efficient Catalytic Removal of Formaldehyde at Room Temperature

Tuning the nitrogen contents in carbon matrix encapsulating Co nanoparticles for promoting formaldehyde removal through Mott-Schottky effect

Highly exposed metal atomic active sites in Al2O3/CoNC: Modify reaction pathways by coupling oxygen species

Exceptional formaldehyde oxidation at room temperature on Co single-atom functionalized TiO 2 nanowires via highly effective O 2 activation

Efficiently catalytic purification of indoor formaldehyde upon Co-N sites derived from ZIF-67 carbonization

FeCo alloy encased in nitrogen-doped carbon for efficient formaldehyde removal: Preparation, electronic structure, and d-band center tailoring

Improved Oxygen Activation over a Carbon/Co 3 O 4 Nanocomposite for Efficient Catalytic Oxidation of Formaldehyde at Room Temperature

Modulating the Coordination of Single Co Atoms to Trigger the Catalytic Oxidation of Formaldehyde at Room Temperature

Catalytic Oxidation of Formaldehyde on Ultrathin Co3O4 Nanosheets at Room Temperature: Effect of Enhanced Active Sites Exposure on Reaction Path

Improved oxygen activation over metal–organic-frameworks derived and zinc-modulated Co@NC catalyst for boosting indoor gaseous formaldehyde oxidation at room temperature

Logical Formulation and In-Situ Assembly of MnCo2O4@MnO2 Nanoflower Arrays on Nickel Foam As Monolithic Catalyst for Formaldehyde Degradation at Indoor Temperature

MnO2-decorated N-doped Carbon Nanotube with Boosted Activity for Low-Temperature Oxidation of Formaldehyde.

Remarkable performance of atomically dispersed cobalt catalyst for catalytic removal of indoor formaldehyde

Promotion of Formaldehyde Oxidation over Ag Catalyst by Fe Doped MnO X Support at Room Temperature

Electrospinning synthesis of Co 3 O 4 porous nanofiber monolithic catalysts for the room-temperature indoor catalytic oxidation of formaldehyde at low concentrations

Catalytic oxidation of formaldehyde on nano-Co 3 O 4 , 2 DCo 3 O 4 , and 3 DCo 3 O 4 catalysts

Pt/NiCo2O4 nanowire arrays on Ni foam as catalysts for efficient formaldehyde oxidation at room temperature

Transition metal-doped modification of lattice defects in formaldehyde catalysts − Controlling the specific surface area and mass transfer

The Catalytic and Adsorptive Synergistic Effect of Oxygen-Vacancy-Rich MnO x /C Catalysts for HCHO Oxidation at Room Temperature

One-step Synthesis of Nanocarbon-Decorated MnO 2 with Superior Activity for Indoor Formaldehyde Removal at Room Temperature