Abstract:In high-temperature aerobic environment, carbon materials have to be protected to delay the oxidation process. In this work, ZrC-TaC coatings were deposited by supersonic atmospheric plasma spraying on ZrC-SiC-coated C/C composites and ablation tests were conducted by oxyacetylene torch under different heat fluxes. When subjected to 4.2 WM/m2 for 20 s, the mass and linear ablation rates of the ZrC-TaC/ZrC-SiC coating system were 0.0076 g/s and 0.0005 mm/s, respectively. In the ablation process, the infiltration of the oxygen and liquid Ta2O5 into the inner layer resulted in significant oxidation of the ZrC-SiC inner layer. Due to the oxidation and microstructure evolution of the ZrC-TaC and ZrC-SiC layers, the porous Zr-Ta-O oxide layer, oxidized ZrC-TaC, and ZrC-SiC layers formed a better chemical combination and showed higher resistance to ablation. However, for a heat flux of 3.2 WM/m2, the molten Zr-Ta-O oxides that have good self-healing ability, were mainly formed on the ablative surface; liquid Ta2O5 together with trace oxygen could penetrate into the inner layers, resulting in the lack of chemical combination between the layers. As a result, the molten oxides were easy to denudate during the ablation and cooling process and showed lower resistance to ablation.

Ablation Behavior of ZrC and ZrO2 Coatings on SiC Coated C/C Composites under Oxyacetylene Torch with Different Heat Fluxes

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

Ablation Behavior of Single and Alternate Multilayered ZrC-SiC Coatings under Oxyacetylene Torch

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Ablation Behavior of ZrB 2 -Based Coating Prepared by Supersonic Plasma Spraying for SiC-Coated C/C Composites under Oxyacetylene Torch

Ablation Resistance of ZrB2–SiC Coating Prepared by Supersonic Atmosphere Plasma Spraying for SiC-coated Carbon/carbon Composites

Ablation Behavior of CVD-ZrC Coating under Oxyacetylene Torch Environment with Different Heat Fluxes

Ablation Behavior of Zrc-La2o3 Coating for Sic-Coated Carbon/Carbon Composites under an Oxyacetylene Torch

Ablative Property and Mechanism of ZrC-TaC/ZrC-SiC Coatings on C/C Composites under Different Heat Fluxes

SiC/ZrB2–SiC–ZrC Multilayer Coating for Carbon/carbon Composites Against Ablation

Microstructure and Ablation Mechanism of SiC-ZrC-Al2O3 Coating for SiC Coated C/C Composites under Oxyacetylene Torch Test

Microstructures and Ablation Resistance of Zrc Coating for Sic-Coated Carbon/Carbon Composites Prepared by Supersonic Plasma Spraying

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

Evaluation of Ablation Resistant ZrC-SiC Multilayer Coating for SiC Coated Carbon/carbon Composites under Oxyacetylene and Laser Conditions

Ablation Resistance of Different Coating Structures for C/ZrB2–SiC Composites under Oxyacetylene Torch Flame

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Supersonic flame ablation resistance of W/ZrC coating deposited on C/SiC composites by atmosphere plasma spraying

Microstructure Characteristics and Ablation Behavior of an Al1.92 Cr0.08 O3-SiC-ZrC Anti-Ablation Coating

Ablation Behavior of ZrC-SiHfOC-MoSi2 Coating for Carbon/carbon Composites under Ar-O2 Plasma Flame

A Multilayer SiC/ZrB2/SiC Ablation Resistance Coating for Carbon/Carbon Composites