Experimental study on preparation of unburned and non autoclaved brick from neutralization slag of lead zinc smelting wastewater

Weiguang LI,Hang YANG,Chongzhi LI,Shifu SHEN,Lijia YE,Youfa LUO
2017-01-01
Abstract:The utilization of neutralization slag from a lead zinc smelting wastewater was investigated to prepare unburned and non autoclaved bricks .On the basis of analysis of main chemical components ,XRD phase analysis and neutralization slag digestion and drying condensation performance analysis .Orthogonal experiment of L16 (4)5 was designed to study the effect of different brick compositions on the strength of 7 d and 28 d of unburned and non autoclaved bricks and the optimum recipe preparation of brick was obtained through the analysis of range and variance ,and the relationship between the molding pressure an d water cement ratio and the properties of unburned an d non autoclaved brick was studied under the optimum formula .The result shows that the factors influencing the 7 d compressive strength of the unburned an d non autoclaved brick were amount of cement ,amount of water slag powder ,amount of mix neutralization slag , amount of fly ash and amount of stone chip in order .The factors influencing the 28 d compressive strength of unburned and non autoclaved brick were amount of mixed neutralization slag ,amount of water slag powder ,amount of stone chip ,amount of fly ash and amount of cement in order .The best experiment formula was 31 .43% mixed neutralization slag ,14 .29% cement ,31 .43% water slag micropowder ,13 .33%fly ash ,9 .52% stone chip ;the best of the ratio of water to cement is 0 .14 ,molding pressure is 20 MPa . Finally ,the 28 d compressive strength of unburned and non autoclaved brick was 27 .7 MPa ,water absorption was 11 .5% ,softening coefficient was 0 .89 and frost resistance index was F25 ,which reached the requirement of JC422-2007non sintered waste tailings unburned brick .
What problem does this paper attempt to address?