Abstract:It is still an urgent task to design metal coatings for the development of corrosion resistance. Herein, Pb-Co-ZrO 2 coating is fabricated on the surface of aluminum plates via one-step pulsed electrodeposition for corrosion resistance. The pulse frequency, current density and duty cycle are 800 Hz, 15 mA cm −2 and 20 %, respectively. In this work, the concentration of ZrO 2 nanoparticles in the bath is the main operating variable. We further explored the deposition mechanism of the nanocomposite coating and demonstrated its application potential in corrosion resistance. As expected, the corrosion resistance and mechanical properties of the coatings increased and then decreased with the increase of the concentration of ZrO 2 nanoparticles in the plating solution. When the concentration of ZrO 2 nanoparticles in the plating solution was 15 g L −1 , the Pb-Co-ZrO 2 nanocomposite coating exhibited excellent corrosion resistance in 3.5 wt% NaCl solution, with an impedance modulus value (5182 Ω cm 2 ) that was eight times higher than that of the pure Pb coating (669 Ω cm 2 ), possessed the highest corrosion potential (- 0.60 V) and the lowest corrosion current density (3.6 μA cm −2 ), while also exhibiting excellent mechanical properties. The mechanism of the improved corrosion performance of the Pb-Co-ZrO 2 composite coatings was further explained using DFT calculations. The results show that the coupling between the interface of Pb-Co solid solution and ZrO 2 nanoparticles effectively improves the overall electron figure of merit of the coatings and triggers an obvious electron localisation, which increases the energy required for the interfacial electrons to escape from the coating interface.

Fabrication and properties analysis of Ni-P coated nanometer ZrO2 composite powders

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Preparation and Magnetic Properties of Nano-nickel Coated Silicon Nitride Composite Powders

Enhanced mechanical properties and corrosion resistance of electro-deposited NiCoP composite coatings with ZrB2 particle addition

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

Fabrication and Characterization of Cobalt Nanoparticles on ZnO Nanorods on a Polished Titanium Substrate

Fabrication and wear property of NiCo coated ZrO2–Al2O3 ceramic particles reinforced high manganese steel-based composites

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Fabrication of NiO/ZrO2 nanocomposites using ball milling-pyrolysis method

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Characteristics and Electrochemical Performance of Ni-coated ZnO Prepared by an Electroless Plating Process

Influence of ZrB2 Nanoparticles on Microstructure and Mechanical Properties of Ni-Co Coating

Strengthening effect of α-ZrP nanosheet inclusions on corrosion resistance and wear resistance of Ni P deposits

Study on Fabrication of Zirconia Nanopowder Plasma-Sprayed Coating

Study of properties of Ni-base nano-ZrO2 composite plating coatings

Preparation and properties of nano ZrO2 coating on magnesium alloy

Preparation of laminar α-ZrP nanosheets enhanced Ni W nanocomposite coating and investigation of its mechanical and anti-corrosion properties

Fabrication of Pb-Co-ZrO 2 nanocomposite coatings and correlation of corrosion mechanisms with electronic work functions

Preparation and properties of Ni-W-P-TiO2 nanocomposite coatings developed by a sol-enhanced electroplating method

Electrodeposition of Ni-P composite coatings: A review

High-temperature oxidation and wear resistance of nano-ZrB 2 reinforced CoNiCrAlY composite coating via a step-fashion mechanical alloying powder process