Abstract:The mechanical performances of ceramic mold are crucial for the quality of casts in investment casting. However, most of the previous researches were focused on the quasi-static performance which is not sufficient for the accurate failure analysis of shell mold under complex stress state. In this investigation, dynamic mechanical behaviors of AI(2)O(3)-SiO2 ceramic shell for investment casting have been studied using split Hopkinson pressure bar (SHPB) at high strain rates Sand pack samples and pure slurry samples were considered for the testing in order to further understand the mechanism of fracture Weibull approach was then applied to describe the strength distribution of ceramic shells. The dynamic increase factor (DIF) of compressive strength increased from 1.23 (863s(-1)) to 2.03 (1959s(-1)) indicating the high dependency of mechanical property to strain-rate. The cross-section and fracture surface were analyzed through scanning electron microscopy (SEM). The microstructural investigations showed that the crack propagation in the ceramic shell is mainly through the weak interface between sand particles and slurry region under quasi-static load At high strain rate, the crack pro pagation path is different which extends through the well sintered slurry region and even runs through the sand particles. The mechanism of crack propagation path is analyzed based on Griffith criterion. In addition, the feature of stress-strain curves indicates the layered structure which plays an important role in the process of fracture.

Dynamic Mechanical Properties of Al_2O_3 Ceramics under Higher Strain-Rate

Compressive properties and failure mechanisms of AlON ceramics under different strain rates

Dynamic Response of Ceramic Shell for Titanium Investment Casting under High Strain-Rate SHPB Compression Load

Experimental Research of Foamed Ceramic Composite under Dynamic Loading Using SHPB

Dynamic material property characterization by using split Hopkinson pressure bar (SHPB) technique

Dynamic mechanical behavior and damage properties of SHCC under high strain rate loading

Dynamic Response Behaviours of Al2O3 Ceramics with Different Grain Sizes under SHPB Compression Loading

Dynamic Properties and Damage Pattern of A95 Ceramic under Low-Impact Velocity

Dynamic compressive properties of 40 vol%SiC_P/2024Al composite

Research on Dynamic Behaviors of A95 Ceramics under Compression

Rapid geometric characterization of ceramics fragments through split Hopkinson pressure bar tests

Dynamic mechanical properties of Alumina prepared by vat photopolymerization based on high solid loading slurry

High strain rate superplasticity in oxide ceramics

Dynamic mechanical properties of W-Zr alloy

Strain-rate effect of polymers and correction methodology in a SHPB test

Effect of Strain Rate and Temperature on Dynamic Mechanical Behavior and Microstructure Evolution of Ultra-High Strength Aluminum Alloy

High-temperature dynamic deformation of aluminum alloys using SHPB

The Dynamic Mechanical Response of Sic Particulate Reinforced 2024 Aluminum Matrix Composites

Dynamic Mechanical Properties and Deformation Mechanism of MB2 Alloy under High Temperature and High Strain Rates

Dynamic Strain Rate Effect of Welds

Dynamic deformation behavior of a high reinforcement content TiB2/Al composite at high strain rates