The Composition and Al-bearing Phases Transition of Cement Paste Subjected to MgSO4 Attack

Qing-jun DING,Kai LIU,Gao-zhan ZHANG,Yang ZHANG,Yi XU

DOI: https://doi.org/10.3963/j.issn.1671-4431.2016.05.001

2016-01-01

Abstract:Under two conditions (7-days cement paste specimen was placed in 5％ MgSO4 solution for 7 d,28 d,90 d and 180 d,respectively;3-days cement paste specimen was placed in different concentration MgSO4 solution),the composition of hydration products and the transformation mechanism of Al-bearing phases were investigated by XRD and 27 Al nuclear magnetic resonance(NMR).The experimental results indicate that the content of CaSO4 · 2H2O and AFt in cement paste,which was placed in 5％ MgSO4 solution for 180 d,significantly increases.The 4-coordinate Al of C-(A)-S-H,the 6-coordinate Al of AFm and TAH transform into 6-coordinate Al of AFt,which cause the specimen expanded destruction.Mg(OH)2 layer formed in the initial erosion stage can suppress 4-coordinate Al of C-(A)-S-H,TAH and AFm transforming into AFt.With the increasing age of erosion,Mg(OH)2 layer was disrupted,the SO42- diffusion rate increased,and the content of AFt significantly increased.The initial MgSO4 erosion stage promotes Al incorporating in C-S-H gel.With the age of erosion extending,AP+ was removed from C-(A)S-H,a large number of 4-coordinate Al transform into 6-coordinate Al of AFt.With the concentration of MgSO4 solution increasing,the dealumination effect of C-(A)-S-H increases,the yield of AFt also increases significantly.