Abstract:The hydraulic concrete structures commonly suffer from severe dissolution. Dissolution has a great influence on the mechanical properties and durability of concrete, which would be detrimental to the normal operation and even cause structure failure. In this study, the effects of an accelerated dissolution method, namely NH4NO3 dissolution, on the microstructure and micro-mechanics of hardened cement pastes have been investigated via X ray fluorescence (XRF), Fourier transform infrared spectrometer (FTIR), X-ray diffraction (XRD), 29Si magic -angle spinning nuclear magnetic resonance (29Si MAS NMR) and microhardness techniques. Besides, an attempt was made to reveal the relationship between the C-S-H microstructure and micro-mechanics of cement paste during the NH4NO3 dissolution process. The results demonstrated that the decalcification process of the cement pastes under NH4NO3 erosion can be classified into two stages. The first stage was the dissolution of Ca (OH)2 in cement pastes. The Ca(OH)2 was almost completely removed, and C-S-H was partly decalcified in this stage. In the second stage, as the C/S of cement pastes decreased to a constant value about 1.83, C-S-H was further decalcified. It was also observed that the continuous dissolution would significantly weaken the micro -hardness of cement pastes. The long-term hydrated cement paste decalcified for 500 min exhibited nearly no microhardness. In addition, the results indicated that the microhardness of the cement pastes was related to the paste C/S, the proportion of Q1 and the polymerization of C-S-H. Finally, it was concluded that the Ca(OH)2 dissolution and degradation of C-S-H structure are the main causes for the degradation of cement pastes under NH4NO3 dissolution.

In Situ Observing the Erosion Process of Cement Pastes Exposed to Different Sulfate Solutions with X-ray Computed Tomography

Nondestructive Monitoring the Deterioration Process of Cement Paste Exposed to Sodium Sulfate Solution by X-ray Computed Tomography

The Variation of Pore Structure in Cement Paste Exposed to Sodium Sulfate Solution with an In-Suit X-ray CT Testing Technology

Numerical Investigation on Gypsum and Ettringite Formation in Cement Pastes Subjected to Sulfate Attack

Impact of Leaching and Chlorides on Sulfate Attack for Cement Paste

3D Meso-Scale Finite Element Modelling on Cement Paste Corroded in Sodium Sulfate with X-ray CT Technique

Microscopic Testing of Sulfur Distribution in Hardened Cement Paste Subjected to External Sulfate Attack

Evaluation of Elastic Modulus of Cement Paste in Sodium Sulfate Solution by an Advanced X-CT–hydration–deterioration Model with SC Method

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Study on sulfur distribution in cement-based materials subjected to external sulfate attack based on Mapping image analysis

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Corrosion Products in Cement-Based Materials under Sulfate Partial Soaking Attack

A Comparable Study on the Deterioration of Limestone Powder Blended Cement under Sodium Sulfate and Magnesium Sulfate Attack at a Low Temperature

The Composition and Al-bearing Phases Transition of Cement Paste Subjected to MgSO4 Attack

Corrosion products of cementious materials under sulfate partial soaking attack

Investigation of Microstructure of C-S-H and Micro-Mechanics of Cement Pastes under NH4NO3 Dissolution by 29si MAS NMR and Microhardness

Deterioration Mechanism of Plain and Blended Cement Mortars Partially Exposed to Sulfate Attack

Effect of Hoop Restraint on the Degradation Behavior of Cement Paste Exposed to Sodium Sulfate Solution

Evolution of a Filling Paste Cementitious System and Impact Patterns of Sulfate Mine Water Erosion on Filling Paste Performance

Monitoring the Evolution of Accelerated Carbonation of Hardened Cement Pastes by X-Ray Computed Tomography

Experimental Study on the Strength Deterioration of Sulfidic Paste Backfill