Abstract:Our research group prepared a new filling paste consisting of steel slag–oil shale residue and no admixtures. It was used as the research object to explore the combined effect of chloride and dry–wet cycling-driven erosion on the long-term stability of a cemented filling paste made of total solid wastes. Macroscopic experiments and microscopic analyses methods were employed. The influence of solutions with different mass fractions of chloride salts and different cycling periods on the uniaxial compressive strength and toxicity of the steel slag–oil shale residue-based filling paste was studied, and the deterioration mechanisms of the steel slag–oil shale residue-based filling paste under combined erosion from chloride and dry–wet cycling were investigated. The test results showed that in the same cycling conditions, the strength of the steel slag-oil shale residue-based filling paste increased first with the increase in the mass fraction of the chloride solution and then decreased with the increase in the mass fraction of the chloride solution after reaching the peak value; the leached concentrations of heavy metal ions decreased with increasing chloride salt mass fraction. With an increase in the number of dry–wet cycles, the compressive strength of the specimens in the chloride salt solution with a mass fraction of 0 (pure water) first increases and then tends to be stable. The strength of samples in 5% and 10% chloride salt solutions increased first and then decreased with an increase in the number of dry–wet cycles. The leached concentrations of heavy metal ions from the samples in all three solutions first decreased and then stabilized. The prehydration products of the steel slag–oil shale residue-based filling paste were C-S-H gels, AFt and Friedel’s salt, and these increased with increasing chloride salt mass fraction and the number of dry–wet cycles. However, the hydration reactions of the samples in the 0% chloride solution nearly stopped in the later stages of cycling, and the samples in 5% and 10% chloride salt solutions developed local cracks due to the accumulation of hydration products. The results showed that the number of dry–wet cycles and the chloride salt mass fraction affected the strength and leaching characteristics of the steel slag–oil shale residue-based filling paste by changing the type and amount of erosion products. The test results provide a scientific basis for the promotion and application of backfilling pastes made from total solid wastes.

Evolution of a Filling Paste Cementitious System and Impact Patterns of Sulfate Mine Water Erosion on Filling Paste Performance

Sedimentation-affected Engineering Performances and Microstructures of a Hybrid Portland- Sulfate Aluminate Cement Grout Cast in Long Tubes

Changes in the Strength and Leaching Characteristics of Steel Slag-Oil Shale Residue-Based Filling Paste in a Complex Erosive Environment

Experimental Investigation on Microstructure and Surface Morphology Deterioration of Limestone Exposed on Acidic Environment

Experimental Study on Microstructure and Erosion Mechanisms of Solid Waste Cemented Paste Backfill under the Combined Action of Dry-Wet Cycles and Sulphate Erosion

Impact of Leaching and Chlorides on Sulfate Attack for Cement Paste

Strength and Leaching Characteristics of Magnesium Phosphate Cement-Solidified Zinc- Contaminated Soil under the Effect of Acid Rain

Experimental Study on Mechanical Properties of Paste Backfill with Flue-Gas Desulphurisation Gypsum under Combined Action of Dry–Wet Cycles and Chloride Erosion

Long-term Properties and Microstructure Change of Engineered Cementitious Composites Subjected to High Sulfate Coal Mine Water in Drying-Wetting Cycles

Mechanical Properties and Deterioration Instability of Filling Body with Gangue-Cement Material Based on AE Experiment

Study on triaxial compression performance and damage characteristics of fiber-reinforced ecological matrix cementing gangue gypsum fill material

Relationship Between Microscopic Pore Structure and Strength of Cement-Based Materials with Low Water-Binder Ratio Under Sulfate Attack Environment

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Study on the leaching of harmful elements and pore characteristics of phosphogypsum-based cemented paste backfill under multi-field coupling interaction

The effect of acid mine drainage on the properties of an all-solid waste paste backfill body based on oil shale residue

The Effect of Wetting–Drying Cycles on the Deterioration of the Physical and Mechanical Properties of Cemented Paste Backfill in Open-Pit Coal Mines

Leaching toxicity and deformation failure characteristics of phosphogypsum-based cemented paste backfill under chemical solution erosion

Effect of environmental pH values on phase composition and microstructure of Portland cement paste under sulfate attack

Properties evolution of calcium sulfoaluminate cement blended with ground granulated blast furnace slag suffered from sulfate attack

Study on the proportion of paste filling materials based on fluorogypsum

Experimental and theoretical investigation on hydraulic fracturing in cement mortar exposed to sulfate attack