Abstract:Portland cement (PC), which has been used as a dominant binder material in concrete since its development, is responsible for approximately 8% of global anthropological CO 2 emissions. Alkali-activated materials, which are based on the activation of precursor materials using alkali activators, are binders developed for environmental gains. The significance of this study lies in exploring the mechanical and microstructure properties of hybrid alkali-activated cements containing PC, produced under various parameters. This investigation provides valuable insights into optimizing the composition and processing conditions for these materials. In this study, 34 mixtures were produced to investigate the Na 2 SiO 3 to NaOH ratio (2, 2.5, and 3), PC substitution level (5%, 10%, 15%, 20%, and 25%) and curing temperature (25, 50, 75 and 100 °C) effects on the hybrid alkali-activated slag/PC components. The highest compressive strength was obtained at 15% PC substitution. As the Na 2 SiO 3 to NaOH ratio increased, the compressive strength of the samples containing 0, 5%, 10% and 15% PC increased. However, the increase in the Na 2 SiO 3 to NaOH ratio negatively affected the compressive strength of the samples containing more than 15% PC. The highest compressive strength in both partially PC-substituted and fully slag samples was achieved when the samples were cured at 50 °C. When the sample containing 100% slag was cured at 50 °C, the degree of hydration was higher compared to the sample cured at 25 °C. In the sample with 15% PC, a sharp band corresponding to the Si–O bond was observed at 25 °C. However, as the curing temperature exceeded 50 °C, this band became broader and weaker. This indicates that the amount of hydration products in the PC-blended alkali-activated slag sample decreased at curing temperatures above 50 °C.

Understanding The Aqueous Phases Of Alkali-Activated Slag Paste Under Water Curing

Recent progress in understanding setting and hardening of alkali-activated slag (AAS) materials

New Insights into Pore Structure and Hydraulic Conductivity of Sodium Hydroxide Alkali-Activated Slag through Advanced Modelling

Research on rheology performance and sealing effect of alkali-activated GGBS paste used for tunnel leakage plugging

Properties and Microstructure of Alkali-Activated Slag Paste Modified by Superabsorbent Polymers

Mechanical properties and microstructure of hybrid alkali-activated cement component

Alkali-activated slag (AAS) paste: Correlation between durability and microstructural characteristics

Properties, mineralogy and microstructure evolution of 4-year calcium silicate slag-based alkali-activated materials

The long-term failure mechanisms of alkali-activated slag mortar exposed to wet-dry cycles of sodium sulphate

Strength Analysis and Optimization of Alkali Activated Slag Backfills Through Response Surface Methodology

Studying the Effect of Alkali Dosage on Microstructure Development of Alkali-Activated Slag Pastes by Electrical Impedance Spectroscopy (EIS)

Hydration characteristics and microstructure development of sodium hydroxide slag pastes exposed under different curing environments

EARLY HYDRATION CHARACTERISTICS AND PASTE STRUCTURE OF COMPLEX BINDING MATERIAL CONTAINING HIGH-VOLUME STEEL SLAG

Effect of alkali contents, moduli and curing time on engineering properties of alkali activated slag

INVERSTIGATION ON THE RELATION BETWEEN SHRINKAGE AND MICROSTUCTURE OF ALKALI ACTIVATED CEMENT

Mechanisms of efflorescence of alkali-activated slag

Compositional, Microstructural and Mechanical Properties of Ambient Condition Cured Alkali-Activated Cement

Study on the Hydration Kinetics and Microstructure of the Sulphate-Alkali Composite Activated Slag Pastes

Hydration and Properties of Slag Cement Activated by Alkali and Sulfate

Effect of Alkali Sulfates in Clinker on Early Setting Behavior of Portland Cement

The Early Age Hydration Products and Mechanical Properties of Cement Paste Containing GBFS under Steam Curing Condition