Abstract:Steel slag is a solid waste generated during the steel-making process. Using steel slag to produce construction materials is an effective way to largely consume this solid waste. However, the high content of P2O5 in steel slag leads to a serious retarding phenomenon in Portland cement, which limits the adding amount of steel slag in the traditional cement and concrete. In this research, with the guiding idea of isostructural effect of Si to P in silica-alumina based system, silica-alumina based cementitious materials composed of steel slag were developed according to different [SiO4] polymerization degree of raw materials. It was found that the steel slag presented an obvious setting retarding effect on ordinary Portland cement, while it did not show the setting retarding effect on silica-alumina based cementitious materials. The compressive strength of silica-alumina based cementitious materials composed of 20-30% steel slag cured for 28 days reached 40 MPa. The hydration products of silica-alumina based cementitious materials composed of steel slag were mostly amorphous C-A-S-H gel, ettringite and Ca(OH)2. As the predominant hydration products, the filamentous and needle-like ettringite and amorphous C-A-S-H gel play a positive role in promoting densification of the paste structure, resulting in strength development in the early hydration process. Moreover, it was observed that the phosphorus in steel slag was involved into the hydration reaction to form C-A-S-H gel. This study points out a promising direction for the proper utilization of steel slag in large quantities. Figure 1 SEM image of hydration products of silica-alumina based cementitious materials composed of steel slag.

Morphological characteristics of hardened paste of complex binder containing high volume of slag

Microstructure of Hardened Complex Binder Pastes Blended with Slag

EARLY HYDRATION CHARACTERISTICS AND PASTE STRUCTURE OF COMPLEX BINDING MATERIAL CONTAINING HIGH-VOLUME STEEL SLAG

Influence of slag on microstructure of complex binder pastes

Early Hydration Characteristics of Complex Binder Containing Slag under High Temperature

MICROSTRUCTURAL CHARACTERISTICS OF COMPLEX BINDER PASTE CONTAINING ACTIVE OR INERT MINERAL ADMIXTURES

Hydration Characteristics of Slag in Cement-Slag Complex Binder

Characteristics of Two Types of C-S-H Gel in Hardened Complex Binder Pastes Blended with Slag

Microstructural Variation of Hardened Cement-slag Pastes Leached by Soft Water

Study on Hydration Degree of Portland Cement-Slag Complex Binders

Influence of Hydration Environment on the Characteristics of Ground Granulated Blast Furnace Slag Hydration Products

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

Influence of Hardened Paste Microstructure on Rheological Property of Cementing Slurries with High Density

Insights into the microstructure and mechanical properties evolution of hydration products in cementitious materials incorporating GGBFS

Long-term Characteristics of the C-S-H Produced by the Hydration of Cement-Ggbs Composite Binder

Hydration Characteristics of Slag-Blended Cement at Different Temperatures

Comparison of hydration properties between cement-GGBS-fly ash blended binder and cement-GGBS-steel slag blended binder

Effect of ultrafine slag on hydration heat and rheology properties of Portland cement paste

Hydration characteristics of silica-alumina based cementitious materials composed of steel slag

Microstructure and Composition of Hydration Products of Ordinary Portland Cement with Ground Steel-Making Slag

A comparison of early hydration properties of cement–steel slag binder and cement–limestone powder binder