Failure research of T-joint at liquefied natural gas tanker

You WANG,Xiaona ZHANG,Hui LI,Shaojie LI,Yu WANG,Guoce ZHANG,Ze ZHANG

DOI: https://doi.org/10.3969/j.issn.1000-6281.2016.05.006

2016-01-01

Abstract:Cracks would generate in the heat?affected zone ( HAZ ) of T?joint and cause leakage when the liquefied natural gas ( LNG) tank was used in low temperature environment for a long time. The low temperature experiments were designed by simulating the service environment of liquefied natural gas ( LNG) tank. The microstructure changes of welded joint HAZ of simulated samples was analyzed using X?ray diffraction, optic microscopy, and scanning electron microscopy. The results show that martensitic transformation is induced in the HAZ by the low temperature ( -196℃) environment. With the increase of the residual stress and the time of immersion in liquid nitrogen, the volume fraction of martensite increases. Comparing with actual failure sample, the vacuum failure of the LNG tank is caused by the increase of martensite at the heat?affected zone of T?joint during the service process. Therefore, reducing stress in the HAZ is beneficial for decreasing the vacuum failure probability of the LNG tank.