Abstract:Crack growth analysis (CGA) was applied to estimate the cycle life of the high-pressure hydrogen equipment constructed by the practical materials of 4340 (two heats), 4137, 4130X, A286, type 316 (solution-annealed (SA) and cold-worked (CW)), and type 304 (SA and CW) in 45, 85 and 105 MPa hydrogen and air. The wall thickness was calculated following five regulations of the High Pressure Gas Safety Institute of Japan (KHK) designated equipment rule, KHKS 0220, TSG R0002, JB4732, and ASME Sec. VIII, Div. 3. We also applied CGA for four typical model materials to discuss the effect of ultimate tensile strength (UTS), pressure and hydrogen sensitivity on the cycle life of the high-pressure hydrogen equipment. Leak before burst (LBB) was confirmed in all practical materials in hydrogen and air. The minimum K-IC required for LBB of the model material with UTS of even 1500 MPa was 170 MPa . mu in 105 MPa. Cycle life qualified 10(3) cycles for all practical materials in air. In 105 MPa hydrogen, the cycle life by K-IH was much shorter than that in air for two heats of 4340 and 4137 sensitive to hydrogen gas embriftlement (HGE). The cycle life of type 304 (SA) sensitive to HGE was almost above 10(4) cycles in hydrogen, while the cycle life of type 316 (SA and CW) was not affected by hydrogen and that of A286 in hydrogen was near to that in air. It was discussed that the cycle life increased with decreasing pressure or UTS in hydrogen. This behavior was due to that K-IH increased or fatigue crack growth (FCG) decreased with decreasing pressure or UTS. The cycle life data of the model materials under the conditions of the pressure, UTS, K-IH, FCG and regulations in both hydrogen and air were proposed quantitatively for materials selection for high-pressure hydrogen storage.

Study of Joule-Thomson Cooling Effect Due to Leakage in Compressed Gas Pressure Vessels

Study on the Joule-Thomson Effect During Leakage in High Pressure Vessels

Study on Heat Transfer Process During Leaks of High Pressure Argon Through A Realistic Crack

Effect of the Joule-Thomson Cooling on the Leak-Before-break Approach

Leak Model and Numerical Simulation of Pressure Vessel Based on Joule-Thomson Effect

Temperature Stability of a Joule–Thomson Microcooler Operating with Pure and Mixed Gases

Numerical Simulation on Hydrogen Induced Cracking Behavior of 4130X Hydrogen Storage Vessel with Defect

Dynamic Response and Crack Propagation of Pre-Flawed Square Tube under Internal Hydrogen-Oxygen Detonation

Damage Assessment of Liquid Nitrogen Filling on Type III Cylinder in Cryo-Compressed Hydrogen Storage Cylinder

Cooling Characteristics of a Nitrogen Micromachined Joule-Thomson Cooler Operating from 88.5 K to 295 K

Crack Growth Analysis Of High-Pressure Equipment For Hydrogen Storage

Failure research of T-joint at liquefied natural gas tanker

Study of Heat Transfer of Cryogenic Methane under Supercritical Pressure with Consideration of Thermal Conduction in Engine Cooling Channel Walls

Experimental Study on the Flow and Thermal Characteristics of Two-Phase Leakage Through Micro Crack

Study on Cooling Capacity Characteristics of an Open-Cycle Joule-Thomson Cryocooler Working at Liquid Helium Temperature

Leak Rates of High Pressure Steam–water Across Simulation Crack

Numerical study of supercritical-pressure fluid flows and heat transfer of methane in ribbed cooling tubes

The Toughness-Induced Crack Deceleration Mechanism on Ultra-High Pressure Steel Gas Pipelines

Experimental Study on Leak Flow Rate Characteristics of High Pressure Subcooled Water Through Axial and Circumferential Microcracks of Steam Generator Tubes under High Back Pressure Conditions

Experimental Research on the Two-Phase Explosive Boiling Mechanism of Superheated Liquid under Different Leakage Conditions

Investigation of heat leakage calculations and experiments for a wide-mouth liquid nitrogen tank