Abstract:The cathode materials of spinel LiMn2O4 coated with 1.5(wt)%Al2O3 and Al doped LiAlxMn2-xO4(x=0.1,0.2,0.3,0.4)were synthesized.The structures and morphologies of the as-prepared materials were characterized by X-ray diffraction(XRD) and Field scanning electron microscopy(FSEM).The results showed that the diffraction of LiMn2O4 modified is similar,with all the peaks index able in the Fd3m space group,but the positions of the diffraction peak shift to higher angle;Al2O3particles appear on the surface of the coated spinel LiMn2O4and powders of Al doped LiMn2O4have the uniform,nearly cubic structure morphology with narrow size distribution which is less than 500nm.Galvanostatic charge-discharge test indicated that cycle performance of LiMn2O4 can be improved significantly after coated or doped.Among all modified samples,LiMn2O4 coated with 1.5(wt)%Al2O3 and LiAl0.2Mn1.8O4had the better electrochemical performance and same initial discharge capacity of 99.7 mAh/g.The capacities retained of 87.4% and 88.4% after 50 cycles,respectively.In initial charge,the EIS of LiAl0.3Mn1.7O4 electrode consist of the semicircle of high frequency region and a arc of low frequency region which continue to narrow as increasing of polarization potential,to evolve into the semicircle at 3.95V and at same time the slash related with the lithium-ion diffusion in the EIS low frequency region emerge.The resistance of SEI film and the thickness of SEI were decrease with the increase of polarization potential,but the charge transfer resistance Rct was first decreasing and then increasing and LiAl0.4Mn1.6O4 had smaller Rct than that of LiAl0.3Mn1.7O4corresponding to the extraction of Li+ions.

Study on Modification of Spinel LiMn2O4 by Overcoating

Surface Modification Mechanism of Spinel Structure LiM_xMn_(2-x)O_4 As Cathode Materials for Lithium Ion Batteries

Study on the Spinel LiMn2O4 Coating with Cobalt Oxide

Surface Modification and Characterization of Spinel LiMn2O4 Coated with MgO

Surface Modification of Li1.03mn1.97o4 Spinels for Improved Capacity Retention

Enhanced Cycling Performance of Spinel LiMn 2 O 4 Coated with ZnMn 2 O 4 Shell

Structure and Electrochemical Performance of Modificated LiMn2O4 by S-Co Codoping and Nano SiO2 Surface Coating

Surface Modification of High Voltage Spinel LiNi 0.5 Mn 1.5 O 4 Cathode Material Manufactured via Co-precipitation

Structure and Electrochemical Performance of Modificated LiMn<sub>2</sub>O<sub>4</sub> by S-Co Codoping and Nano SiO<sub>2</sub> Surface Coating

Synthesis and Electrochemical Performance of Spinel LiMn<sub>2</sub>O<sub>4</sub> Modified by CNTs

Novel method to enhance the cycling performance of spinel LiMn2O4

Electrochemical Performance of Spinel LiMn_2O_4 Modified

Co3+-Modified Surface of Limn2o4 Spinel for Its Improvement of Electrochemical Properties

Synthesis and electrochemical performance of spinel LiMn2O4 modified by CNTs

Enhanced Cycling Stability of LiMn2O4 by Surface Modification with Melting Impregnation Method

Enhanced electrochemical performances of 5 v spinel LiMn 1.58Ni0.42O4 cathode materials by coating with LiAlO2

Effect of Co 3+ Doping on Crystal Structure and Electrochemical Properties of Spinel LiMn 2 O 4 Cathode Material

Study on improvement of cycle performance of spinel LiMn2O4

Boosting the cycling performance of spinel LiMn2O4 by in situ MnBO3 coating

Research on LiNi_xMn_(2-x)O_4 Surface Modification of LiCoO_2 As Cathode Materials for Li-ion Batteries

Structure and Electrochemical Performance of Spinel Limn1.95ni0.05o3.98f0.02 Coated with Li-La-Zr-O Solid Electrolyte