Effect of temperature on mechanical behavior of Cu–Cr–Co–Ti alloys
Jiajun Zhang,Siruo Zhang,Xinghao Cao,Longjian Li,Xiong Yang,Zongning Chen,Enyu Guo,Huijun Kang,Rengeng Li,Tongmin Wang
DOI: https://doi.org/10.1016/j.matchar.2023.112904
IF: 4.537
2023-04-14
Materials Characterization
Abstract:In this study, high-performance Cu–0.69Cr–0.46Co–0.34Ti (wt%) alloys with nano-precipitates and nanotwins are prepared via a two-step cryorolling and aging process. The effects of Co and Ti on the microstructural evolution as well as room-temperature and elevated-temperature mechanical behaviors are investigated. The results show that the two-step process produces high-density dislocations, profuse nanotwins into Cu–Cr–Co–Ti alloys, and enhances the mechanical properties of the latter significantly. The high-density dislocations provide sufficient diffusion paths for Cr atoms and accelerate the transformation of Cr precipitates from face-centered cubic (fcc) to body-centered cubic (bcc), resulting in the co-existence of coherent fcc Cr and incoherent bcc Cr precipitates. Dislocation strengthening and Orowan precipitation strengthening contribute significantly to the strength of the Cu–Cr–Co–Ti alloys. The tensile strength (643 MPa), hardness (201 HV), and electrical conductivity (64.75% IACS) of samples subjected to the two-step process are obtained. Results show that a CoTi compound shell inhibits the diffusion of external Cr atoms to the core and restrains the coarsening of Cr precipitates. Meanwhile, stable nano-precipitates and nanotwins decelerate the progress of recrystallization, thus improving the elevated-temperature mechanical behavior.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing