Abstract:Cu-Be alloys exhibit excellent comprehensive performance in electrics, thermotics, and mechanics, and hence, they attract much attention. Among them, low-Be copper alloys are more environmentally friendly and promising. This study explores the effects of different Ni contents and heat treatment parameters on the properties, microstructures, and precipitates of Cu-0.2 wt% Be-x wt% Ni (0 < x < 2.0) alloys. The experimental results demonstrate that the fast cooling rate of cast alloys during solidification contributes to retention of the solute atoms in the copper matrix, which is beneficial for subsequent solid solution treatment. Furthermore, solid solution treatment slightly reduces the electrical conductivities, microhardness values, and compressive yield strengths of Cu-0.2 wt% Be-1.0/1.6 wt% Ni alloys. The optimal solution temperature and time are about 925 ℃ and 60 min, respectively. Aging treatment significantly increases the electrical conductivities, microhardness values, and compressive yield strengths of Cu-0.2 wt% Be-1.0/1.6 wt% Ni alloys. The best aging temperature is around 450 ℃. However, the properties of Cu-0.2 wt%Be-0.4 wt%Ni alloys remain unaffected by solution and aging treatments. Around x = 1.0, Cu-0.2 wt% Be-x wt% Ni alloys possess the best comprehensive properties, which are about 72%IACS of electrical conductivity, 241 HV of microhardness, and 281MPa of compressive yield strength, respectively. TEM and EDS analyses reveal that the precipitate evolution of Cu-0.2 wt% Be-1.0 wt% Ni alloys with aging time is GP zones → γ″ → γ'. Notably, a distinct double-peak age strengthening phenomenon emerges with Cu-0.2 wt% Be-1.0/1.6 wt% Ni alloys. The precipitation of plenty of GP zones at the early stage of aging should account for the first strengthening peak, and the strengthening mechanism transformation of the γ″ or γ' phase from shear to Orowan should induce the second strengthening peak. This work may help to design new low-Be copper alloys and their preparation processes.

A Cu-Ni-Ti Alloy with Excellent Softening Resistance Combined with Considerable Hardness and Electrical Conductivity Obtained by the Traditional Aging Process

The Effect of Al on Microstructure and Properties of Cu-15Ni-8Sn During the Aging

Effects of aging treatment on mechanical and electrical properties of Cu-Co-(Ti) alloys

Microstructure and mechanical properties of a CuNiTi alloy with a large product of strength and elongation

Microstructure and Mechanical Properties of a High Strength Cu-Ni-Si Alloy Treated by Combined Aging Processes

Effects of Ti Addition on Microstructure, Mechanical Properties and Corrosion Resistance of the Cu-Zn-Ni Alloy

A Novel Microstructure of Cu-Ti Alloy with Ultrahigh Electrical Conductivity and Strength

Effects of Fe Content on Properties and Microstructure of Cu–Ti Alloys During Aging

Effects of Ni content on microstructure and properties of aged Cu−0.4Be alloy

Effects of Ni Content and Heat Treatment on the Properties, Microstructures, and Precipitates of Cu-0.2 wt% Be-x wt% Ni Alloys

Accelerating heterogeneous nucleation to increase hardness and electrical conductivity by deformation prior to ageing for Cu-4 at.% Ti alloy

Comparative Studies on Microstructures and Properties of Cu–Ni–M Alloys Controlled by Strong Interaction Between Elements

A Novel Cu-10Zn-1.5Ni-0.34Si Alloy with Excellent Mechanical Property Through Precipitation Hardening

Microstructure Evolution and Mechanical Property of Cu-15Ni-8Sn-0.2Nb Alloy During Aging Treatment

Precipitation Behavior and Performance Evolution of Cold-Rolled Cu-Ti-fe Alloy During Heat Treatment

Microstructure and Properties of High-Conductivity, Super-High-strength Cu–8.0Ni–1.8Si–0.6Sn–0.15Mg Alloy

Microstructural Evolution, Phase Transition, and Physics Properties of a High Strength Cu–Ni–Si–Al Alloy

Microstructure and Property Evolution of Cu–9Ni–6Sn-xCr Alloys During Thermo-Mechanical Treatment Process

Thermomechanical Treatment of Super High Strength Cu-5.2Ni-1.2Si Alloy

Microstructure and Precipitate Evolution in Cu-3.2Ni-0.75Si Alloy Processed by Twin-Roll Strip Casting

Microstructure evolution and aging hardening in a Cu-25Ni-25Mn alloy