Microstructural Evolution, Phase Transition, and Physics Properties of a High Strength Cu–Ni–Si–Al Alloy

Qian Lei,Shengyao Li,Jialun Zhu,Zhu Xiao,Feifei Zhang,Zhou Li
DOI: https://doi.org/10.1016/j.matchar.2018.11.018
IF: 4.537
2018-01-01
Materials Characterization
Abstract:Cu-6.0 Ni-1.0 Si-0.5 Al (wt%) alloy was fabricated, and its phase transformation behavior in the early stages of aging treatment were studied systematically, including the mechanical properties, type of precipitates, formation heat of precipitates, elastic strain energy, crystal orientation relationships, and spatial distribution of elements. The experimental results demonstrate that a B2 ordering structured j3-NiAl precipitate formed in the matrix as the supersaturation solid solution (SSS) was aged at 400 degrees C; 8-Ni2Si, a L1(2) ordering structured beta-Ni3Si, and L1(2) structured gamma'-Ni3Al were precipitated from the matrix aged at 450 degrees C; and discontinuous delta-Ni2Si precipitates occurred in the matrix aged at 500 degrees C and above. Atom probe results revealed that Ni and Si formed clusters with a size of 1-2 nm, and Al tended to segregate around these clusters as the SSS was aged at 450 degrees C. The ultimate tensile strength of the studied alloy was 1080.2 +/- 20.4 MPa for the sample aged at 450 degrees C for 1 h, and the electrical conductivity was 25.4% IACS. Sketch maps of the crystal orientation relationships between the matrix and precipitates were also established.
What problem does this paper attempt to address?