Effects of binders on properties of composite fabrics with nanofibers

Xin XIA,Meng-jia CAO,Ling CHEN

DOI: https://doi.org/10.3969/j.issn.1671-024x.2016.04.001

2016-01-01

Abstract:In order to improve the properties of wearability and the quality of interface adhesion of composite fabric with nanofibers, plasma treatment was used as preprocess, and the optimal parameter of plasma treatment was decid-ed by the dynamic contact angle test. It was carefully studied the effects of three different binders i.e. melting ad-hesive film using low temperature, fibrous binder and aerogel on the heat preservation property, the air perme-ability and water vapor permeability, as well as the mechanical property of composite fabrics. The results showed that the optimal parameter of plasma treatment is power 120 W and treating speed 80 mm/s;the best heat preser-vation property was obtained by using aerogel as the binder, and the heat transfer coefficient of composite fabric is 12.37 w/(m2·℃), the thermal insulation coefficient is 39.26%, and%CLO value is 0.521(0.155℃m2/W);the excellent air permeability and water vapor permeability properties and the high quality of interface adhesion of composite fabric were obtained by using melting adhesive film, and the air permeability rate of composite fabric is 11.42 mm/s, water vapor permeability 17 010.2 g/(m2·d), and the peeling strength 53.75 cN;what′s more, it is discovered that the morphologic structure and distribution of the binder in the interface are the main influence factors on the properties of composite fabric.