Effects of Dowel Rotation Welding Conditions on Connection Performance for Chinese Fir Dimension Lumbers
Xiao Zhong,De Li,Xiaoxue Xu,Quan Li,Danyun Yu,Zhigang Wu,Jiankun Liang,Jun Peng,Wen Gu,Xin Zhao,Shuang Yin,Guifen Yang,Feiyan Gong
DOI: https://doi.org/10.3390/f15061038
IF: 3.282
2024-06-16
Forests
Abstract:In this study, the rotating welding process of Chinese fir (Keteleeriafortunei) in Guizhou, China, was systematically analyzed. The effects of rotating welding conditions, including the dowel-to-guide hole diameter ratio, welding time, depth, base surface, angle, and dowel type, on the performance of welded Chinese fir were explored. Moreover, the physical and chemical changes oftheChinese fir interface during welding were revealed by Fourier-Transform Infrared Spectroscopy (FT-IR), X-ray Photoelectron Spectroscopy (XPS), X-ray Diffraction (XRD), and Scanning Electron Microscopy (SEM). The results indicated the following: (1) The rotating welding technology can quickly achieve a strong connection between wood through friction heat without chemical adhesives and compared with traditional wood connection technology such as gluing or mechanical fixing;it has the advantages of simple operation, high production efficiency; and environmental friendliness. (2) Aftertherotating welding, the wood underwent significant pyrolysis, especially the degradation of hemicellulose. The heat generated in the welding process caused good melting and mechanical interlocking between the dowel and the wall of the guide hole, but it was also accompanied by afriction loss of the dowel and the substrate. (3) The welding parameters affected the wood's connection strength and stability by altering heat production, distribution, transfer, and frictional losses. The impact of the dowel-to-guide hole diameter ratio had a great influence on the connection strength. When the diameter ratio was 1:0.7, the tensile strength was the highest, reaching 2.27 MPa. (4) The analyses of XPS, FTIR, XRD, and SEM proved thatthechemical composition changes at the interface, leading to a more structured crystalline bond and enhanced connection strength due to fiber entanglement and interlocking. This research providesatheoretical and experimental basis forthefurther innovation and development of wood processing technology and provides a new technical path forthegreen manufacturing of wood structure buildings.
forestry