Effects of Zinc Bath Temperature on Microstructure of Hot Dip Galvanized 0.49%si Reactive Steel
KONG Gang,LIU Ren-bin,CHE Chun-shan,LU Jin-tang
DOI: https://doi.org/10.3969/j.issn.1001-4381.2011.01.018
2011-01-01
Journal of Materials Engineering
Abstract:The hot dip galvanized samples of high silicon reactive steel(0.49%Si,mass fraction) were prepared by immersed in molten zinc bath at different temperatures(440,480,520,560,600℃) for different time(1,3,5,10min).The effects of zinc bath temperature and immersion time on the galvanized coatings were discussed.SEM/EDS results show that at 440℃ and 480℃,the coating is composed of thin δ layer and lumpy ζ phase.No Γ phase is found.The excessive growth of ζ produces an undesirable coating with excessive thickness,gray appearance and bad adhesion.The growth rate of coating obeys by interfacial reaction mechanism.At 520℃,the coating is composed of extremely thin Γ layer,compact δk layer and loose δp layer.The growth rate of coating is controlled by diffusion mechanism.At 560,600℃,the coating is a Γ layer and a compact δ layer.Some δ particles are dispersed in η layer.The growth rate of coating is controlled by diffusion mechanism,accompanying the dissolve of δ from coating into molten zinc bath.The optimized operating temperature for high temperature galvanizing should be controlled in the range of 520-560℃.