Microstructure and Corrosion Resistance of Hot-Dipped Zn-Ti Coating

Xu Qiao-yu,Gui Yan,Lu Jin-tang,Kong Gang,Che Chun-shan

DOI: https://doi.org/10.3321/j.issn:1000-565X.2008.07.017

2008-01-01

Abstract:In order to restrain the excess growth of the coatings induced by reactive steel containing silicon during the hot-dipped galvanizing process,Ti was added in a Zn bath with a mass fraction of less 0.1%,and the microstructures of the coatings on the steel containing 0.09% of Si were investigated.Then,the corrosion resistances of Zn and Zn-Ti coatings were studied by means of the neutral salt spray test,the electrochemical polarization and the X-ray photoelectron spectrum.The results show that,with the increase of the Ti content in Zn bath,the growth of ζ phase in the coating is obviously restrained,the excess growth of the coating is thus effectively restrained,and the thickness of ζ+δ phase gradually decreases.It is also indicated that there arise Γ2 particles when the Ti content in Zn bath is more than 0.05%,that the Zn-Ti coating in 5% NaCl solution is of lower corrosion current,larger polarization resistance,less spontaneous corrosion tendency and better corrosion resistance than pure Zn coating,and that the oxidized film of Zn-Ti coating is composed of ZnO and TiO2.As a result,the excellent corrosion resistance of Zn-Ti coating is due to the presence of steadier TiO2 film on the coating surface.