Abstract:A Zn-Sn coating of ~30 μm thickness was prepared on an iron substrate by mechanical deposition using zinc and tin powders as raw materials. The Zn-Sn coating consists of zinc powder particles physically stacked with tin powder particles and filled with reduced tin, and the tin content in the coating is 20%–30%. The resulting Zn-Sn coating was characterized and analyzed with scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), polarization curves (Tafel), electrochemical impedance (EIS), and energy dispersive X-ray spectrometry (EDS). The results showed that the Zn powder was co-deposited with the Sn powder in a portable manner and the Sn powder was deflected and deformed to a great extent. The spot-flocculated reduced Sn also covered the surface of the Zn powder to fill the interstices of the coating to make the coating more compact. Compared with the pure Zn coating, the Zn-Sn coating has a positive shift of 68 mV in the self-corrosion potential in the polarization test, and the corrosion current was only 20% of that of the pure Zn coating. The reduced Sn had a shielding effect on the Zn powder and at the same time, in combination with inert tin powder, the polarization resistance of the plated layer increased to 1118 Ω/cm2. Furthermore, compared to the pure zinc layer, the time of white rust and red rust increased by 24 and 240 h, respectively. In addition, the XPS results showed that the Zn-Sn plating layer was clearly passivated, which was mainly due to the formation of Zn(OH)2 and Sn(OH)2. The results also emphasized that the tin element in the Zn-Sn plated layer can maintain the morphology of zinc powder, compact the plating layer, and prevent the release of corrosion products, thus improving the corrosion resistance of the Zn-Sn coating.

Effect of Electrodeposited Ni Layer on the Galvanized Coatings of Reactive Steels

In-situ Zn-Al Layered Double Hydroxide Conversion Coatings Prepared on Galvanized Steels by a Two-Step Electrochemical Method

Effect of Ni-interlayer on zinc-assisted liquid-metal-induced-embrittlement susceptibility of 22MnB5 galvanized steel

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

The inhibition of MnO on Fe 2 Al 5 Zn x growth and associated three-dimensional nested phase distribution in the galvanized coating of high-Al low-Si dual phase steel

Effect of Zinc Immersion Pretreatment on the Electro-Deposition of Ni Onto AZ91D Magnesium Alloy

The Performance of Zn-Ni Alloy Coating Electrodeposited from Stabilized Bath

Electroplating and Physicochemical Properties of Zinc–Nickel Alloy Coatings from Ammonium Oxalate Electrolytes

Electrodeposition of decorative and protective Zn–Fe coating onto low-carbon steel substrate

Effect of Ni on the oxidation behavior of corrosion products that form on low alloy steel exposed to a thin electrolyte layer environment

ZINC-NICKEL ALLOY ELECTROPLATING IN AN ALKALINE BATH

Effects of Si Addition on Interfacial Microstructure and Corrosion Resistance of Hot-Dip Zn–Al–Mg–Si Alloy-Coated Steel

Influence of Phase Composition of Zn–Ni Alloy Film on the Corrosion Resistance of Zinc Coating

Effects of Al contents on microstructure and properties of hot-dip Zn-Al alloy coatings on hydrogen reduced hot-rolled steel without acid pickling

Study on the interface reaction layer of hydrogen reduction hot-rolled high-strength steel hot-dip galvanizing

Electroplating Behavior of Zn-Ni Alloys in an Alkaline Electrolyte

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Study on Microstructure and Properties of Mechanically Deposited Zn-Sn Coating

Influence of Electrodeposition Conditions on the Microstructure and Corrosion Resistance of Zn–Ni Alloy Coatings from a Deep Eutectic Solvent

Influence of pretreatments on physicochemical properties of Ni-P coatings electrodeposited on aluminum alloy

The effect of surface preparation on the nucleation of zinc-nickel alloy electroplated in acidic electrolyte on steel substrate