Effect of Adding Lanthanum (la3+) on Surface Performance of Ni-P Electroless Plating Coatings on RB400 Support Anchor Rod Steel
Ruizhen Xie,Hongyan Zhang,Jiaojuan Zou,Naiming Lin,Yong Ma,Zhenxia Wang,Wei Tian,Xiaofei Yao,Pengju Han,Zhihua Wang,Bin Tang
DOI: https://doi.org/10.1016/s1452-3981(23)17398-6
IF: 1.541
2016-01-01
International Journal of Electrochemical Science
Abstract:Anchor rod, a common support material in engineering which is often used in civil engineering structures, such as roadway, mines, underground tunnels and rock slope supporting and so on. Owing to the complex service environment and condition, the anchor rod is susceptible to wear and corrosion. In order to improve the wear and corrosion resistance of anchor rod and increase the service lifetime during operation, Ni-P coatings have been prepared on RB400 anchor rod steel via electroless plating. Rare earth element of Lanthanum (La3+) with various concentrations have been added into the electroless plating solution. The surface morphologies, phase constitutions and cross-sectional composition distributions of phosphorus contents in the coatings were characterized by scanning electron microscope (SEM), X-ray diffraction (XRD) and glow discharge optical emission spectroscope (GDOES). Tribological performance and corrosion resistance of the obtained Ni-P coatings were investigated by reciprocating wear testing machine and electrochemical workstation. The results showed that the La3+ which played an important role on refining and modifying grain, had significantly influences the properties of Ni-P coatings. In terms of wear resistance, 0.25 g/L is the optimum supplementation, but the effect of La3+ on the wear resistance is not significant. While the La-coatings with outstanding corrosion resistance exhibit the highest corrosion potential, lowest corrosion current density and maximum resistance value between solution and substrate when the supplementation is 0.50 g/L.