Abstract:This study was focused on the long-term corrosion performance of coated AA2024 and AA5119 aluminum alloys in the atmosphere and coastal environment after 4, 8 and 12 years of exposure. Structural analyses of samples using SEM and XRD analyses revealed that the corrosive surface area of alloys increased with increasing the atmospheric exposure time, and formation of Al(OH)3 as corrosion product on the corroded surface layer of both atmospheric exposed 12 years samples. Comparison between the exposed 12 years samples showed that the higher level of impurities, deeper pits and exfoliation corrosion were observed for exposed AA2024 sample which related to the destruction of anodic oxide film due to pitting attack and decrease of protection capability of the epoxy coated layer, and lower level of impurities and corrosion on the AA5119 sample can be related to the presence of lower Si/Mg molar ratio in the alloy. Electrochemical impedance studies showed the decrease in corrosion resistance with the increase in the duration of atmospheric exposure. Results also showed that deposition of corrosion products on the surface of AA5119 alloy can act as a protective layer through preferentially filling the pores/defects. Therefore, the observations indicate the corrosion resistance of aluminum alloys is significantly dependent on the composition and created crystal defects in the manufacturing process of alloys. Coated AA5119 aluminum alloys show a higher corrosion resistance than that AA2024 in long-term atmosphere exposure in the coastal environments.

Corrosion behavior of rare earth sealing anodized coating on aluminum alloy LY12

Electrochemical study of the corrosion behavior of Ce sealing of anodized 2024 aluminum alloy

Studies on the process and property of rare earth sealing for anodized LY12 aluminum alloy

Corrosion resistance of anodically oxidized LY12 aluminum alloy after modification with cerium nitrate and silane

Anti-corrosion Performance of LY12 Al Alloy Reinforced by Anodic Oxidization and Silanization

Corrosion Behaviour of Ly12 Alloy under Thin Electrolyte Films

Study of double layer rare earth metal conversion coating on aluminum alloy LY12

Study of mixed rare earth metal (REM) conversion coating on aluminum alloy LY12

Rare Earth Application in Sealing Anodized Al-Based Metal Matrix Composites

Corrosion of Ly12 Aluminum Alloy in Sodium Chloride Solution

Electrodeposition of aluminum on rare earth alloy surface in room temperature molten salts

Electrochemical Study of Corrosion Behavior of Rare Earth Based Chemical Conversion Coating on Aerospace Aluminum Alloy

Study on the rare earth sealing procedure of the porous film of anodized Al6061/SiCp

Electrochemical features during pitting corrosion of LY12 aluminum alloy in different neutral solutions

Hydrothermal and cerium salt sealing of a 6061 aluminum alloy

Study on Inhibition Behavior of Aluminum-Based Detergent

ELECTROCHEMICAL FEATURES OF THE CORROSION OF AN ALUMINUM-LITHIUM ALLOY IN 3.0% NaCl SOLUTION

Performance of Anodic Films Formed on Lead Based-Rare Earth Alloys As Positive Grid

Investigation of Long-term Corrosion of AA2024 and AA5119 Aluminum Alloys under chromate coating in Marine Atmosphere by Electrochemical Impedance Technology

Corrosion Behavior of Aluminum Bronze under Thin Electrolyte Layers Containing Artificial Seawater

Exfoliation Corrosion of Al-Li Alloy 2090-T6 in Exco Solution: A Study of Electrochemical Noise and Electrochemical Impedance Spectroscopy