Effect of CeO2 on microstructure and properties of wear and corrosion resistance martensitic stainless steel‐based coating on laser cladding
Fang Zhao,Tieming Guo,Yiwen Zhang,Xiaohong Wei,Ruihua Zhang,Xueli Nan,Kang Dong,Derong Hu
DOI: https://doi.org/10.1002/srin.202200398
IF: 2.1258
2022-09-11
steel research international
Abstract:The effects of CeO2 on the quantity, morphology and distribution of carbides, the microhardness, friction and wear properties and corrosion resistance of 0.3C‐16Cr martensitic stainless steel‐based cladding layer is investigated. The results show that the addition of CeO2 inhibits the dendrite growth and improves the morphology, size, and distribution of carbides in the cladding layer, the hardness shows a peak with the increase of CeO2 content, the wear rate of the cladding layer with CeO2 decreases and the wear resistance increases. In addition, the addition of CeO2 significantly improves the corrosion resistance of the cladding layer, causing the pitting potential to increase, and the blunt current density to decrease. Compared with the original sample, the wear amount and dimensional blunt current density of the sample with 0.3% CeO2 content were reduced by 55.36% and 35.32%, respectively, and the pitting potential was increased by 2.71 times, the comprehensive performance of the cladding layer was the best. This is mainly because CeO2 can increase the latent heat of crystallization during cooling process of the cladding layer, reduce the constitutional supercooling, inhibit the directional growth of dendrites, improve the uniformity of the microstructure and composition, thereby improving the wear resistance and corrosion resistance. This article is protected by copyright. All rights reserved.
metallurgy & metallurgical engineering