Nucleation and strengthening mechanism of laser cladding aluminum alloy by Ni-Cr-B-Si alloy powder based on rare earth control

Chao Jie Liang,Cheng Lei Wang,Ke Xiang Zhang,Mu Lin Liang,Ying Guang Xie,Wei Jie Liu,Ji Jie Yang,Sheng Feng Zhou

DOI: https://doi.org/10.1016/j.jmatprotec.2021.117145

IF: 6.3

2021-08-01

Journal of Materials Processing Technology

Abstract:<p>To improve the comprehensive performance of aluminum alloy and expand its application range, a laser cladding technology was used to a prepare Ni-Cr-B-Si alloy cladding layer, adding 4% CeO₂, 5% Y₂O₃, and 5% La₂O₃ on the surface of 6063Al. The distribution of elements, the nucleation and growth mechanism of the interface transition and upper cladding layers, and the action mechanism of rare earths were analyzed from the thermodynamics, kinetics, and solidification perspectives. Results show that the cladding layer is mainly composed of a thin interface transition layer at the bottom and a thick cladding layer at the top. There are numerous pores and cracks in the interface transition layer of the Ni-Cr-B-Si cladding layer, part of the cladding layer is peeled off, and the structure is obviously segregated. However, the cladding layer adding with 4% CeO₂, 5% Y₂O₃ and 5% La₂O₃ has no obvious pores, cracks and shedding, its grain distribution is more dispersed, and the structure is refined. The organization state from good to poor follows the order Ni60 + 4%CeO₂ cladding layer, Ni60 + 5%Y₂O₃ cladding layer, and Ni60 + 5%La₂O₃ cladding layer. It was found through research that the addition of rare earth can improve the fluidity of the molten pool during the solidification of the cladding layer and purify the molten pool, and most of the rare earths are segregated at the grain boundary and phase boundary, which strengthens the grain boundary and phase boundary. The strengthening mechanism of the cladding layer is solid solution strengthening and fine grain strengthening, and the Ni60 + 4% CeO₂ cladding layer also has a strengthening mechanism of dispersion strengthening.</p>

materials science, multidisciplinary,engineering, manufacturing, industrial

What problem does this paper attempt to address?

The problem this paper attempts to address is the preparation of Ni-Cr-B-Si alloy coatings on the surface of 6063 aluminum alloy using laser cladding technology, with the addition of 4% CeO₂, 5% Y₂O₃, and 5% La₂O₃ rare earth oxides to improve the comprehensive performance of the aluminum alloy and expand its application range. Specifically, the paper focuses on the following aspects:

1. **Improving the comprehensive performance of aluminum alloy**: By preparing Ni-Cr-B-Si alloy coatings on the surface of aluminum alloy using laser cladding technology and adding rare earth oxides to improve the hardness, wear resistance, and corrosion resistance of the aluminum alloy.

2. **Addressing defects in the laser cladding process**: During the aluminum alloy melting process, defects such as pores and cracks are prone to occur. The paper studies the effect of adding rare earth oxides on these defects, aiming to reduce or eliminate these issues.

3. **Analyzing the mechanism of rare earth elements**: From the perspectives of thermodynamics, kinetics, and solidification, the paper analyzes the distribution, nucleation, and growth mechanisms of rare earth elements in the interface transition layer and upper coating, as well as the enhancement effect of rare earth elements on the coating performance.

4. **Optimizing the coating structure**: By adding different types and contents of rare earth oxides, the paper studies their impact on the microstructure of the coating, particularly the improvement of grain refinement and structural uniformity.

Through experimental and theoretical analysis, the paper explores the role of rare earth elements in the laser cladding process, aiming to provide effective solutions for improving the surface performance of aluminum alloys.