Mechanical and corrosion resistance of laser cladding Ni-based alloy of steel plate under variable defocusing

Guo-ye Jiang,Yu-ping Liu,Jin-lei Xie,Wu-chang Wang

DOI: https://doi.org/10.1016/j.ijleo.2020.165464

IF: 3.1

2020-12-01

Optik

Abstract:<p>The laser-clad nickel-base superalloy Ni35 powder is tested on Q235 steel by YLS-3000 fiber laser. Under other conditions, the defocus amount (30 mm and 50 mm) is changed to observe the effect of it to the mechanical heat stability of the cladding layer. Compared with the substrate, the cladding layer formed by laser cladding exhibits better mechanical properties and corrosion resistance as a whole. The mixed morphology of the cladding layer and the matrix is similar to "mushroom shape"; With the defocus amount increasing, the fusion angle α between the cladding layer and the substrate is increased, and the microstructure becomes more refined, thereby the hardness of the cladding layer is increased, and the corrosion resistance is enhanced. After heat treatment to 600 °C, the crystal grains are further refined, and both the maximum and the average hardness of the cladding layer are increased. The cladding layer exhibits favorable stability. The cladding layers at 30 mm and 50 mm defocusing exhibit good mechanical thermal stability, corrosion resistance, and high temperature adaptability. The cladding layer with high defocusing performance is superior.</p>

optics

What problem does this paper attempt to address?

This paper aims to study the influence of defocus amount on the quality of nickel - based alloy cladding layer on Q235 steel plate in laser cladding technology, including aspects such as macro - morphology, microstructure, micro - hardness and corrosion - resistant performance. Specifically, by changing the defocus amount parameters (30 mm and 50 mm) in the laser cladding process, the mechanical - thermal stability, corrosion resistance and high - temperature adaptability of the cladding layer under different defocus amounts are observed. In addition, the performance changes of the cladding layer before and after heat treatment are also compared to determine the most suitable laser cladding parameters.

The main conclusions of the paper are as follows:

1. As the defocus amount increases, the horizontal cladding width of the cladding layer increases, and the vertical cladding depth decreases; the fusion angle between the cladding layer and the substrate boundary changes from \( \alpha = 0 \) to \( \alpha > 0 \); grain refinement increases the hardness of the surface and interior of the cladding layer. The mixing form of the cladding layer and the substrate is similar to "mushroom - like", and the hardness of the cladding layer is higher than that of the substrate. When the defocus amount is 30 mm, pores appear in the cladding layer; under the same defocus amount, the grain size of the cladding layer gradually increases from top to bottom.

2. The corrosion - resistant performance of the cladding layer is better than that of Q235 steel. As the defocus amount increases, the corrosion - resistant performance of the cladding layer is enhanced. Under the experimental conditions, neither the cladding layer nor the substrate forms an obvious passive film in the Cl - solution.

3. After heat treatment, the grains are more refined than at room temperature, and the inter - granular spacing increases. The maximum hardness and the average hardness are improved compared with those at room temperature, indicating that the cladding layer formed by laser cladding high - temperature nickel - based alloy powder on the surface of Q235 steel has better adaptability and mechanical stability under high - temperature conditions.

In conclusion, through systematic research, this paper reveals the important influence of defocus amount on the quality of laser cladding layer and provides a theoretical basis for further optimizing the laser cladding process.