Microstructure and corrosion resistance of laser clad ferrite-based coatings with rare earth La2O3

GaoMin Zhao,Kunlin Wang

2003-01-01

Abstract:The Ferrite-based alloy powders with different contents of La 2O3 were laser-clad onto steel substrate. The microstructural features and phase structure of these coatings were studied by scanning electron microscope (SEM) and X-ray diffraction (XRD), respectively. The results showed that me microstructure of the coatings with La 2O3 was refined and purified and the main phase of the coatings was γ (Fe,Ni). Moreover, the electrochemical properties of the coatings were investigated by anodic polarization curves and electrochemical impedance spectroscopy (EIS). Anodic polarization results indicated that both polarization potential and polarization current density were reduced with the addition of La2O3. EIS results showed that, with the increasing of La2O3, the inductive arcs shrunk and capacitive arcs expanded. The inductive arc at low frequency was disappeared and fully changed to capacitive arc when the La2O3 addition reached 1.2wt%. The corrosion weight loss experimental results showed that the corrosion rate was lower and the corrosion attack was lighter in the coatings with La2O3 than that without La2O3, resulting in a substantial improvement of the corrosion resistance.