Experimental Research on Preparation of Zinc Ferrite by Roasting

Ming XU,Jin-lin YANG,Shao-jian MA,Li-ji BAI,Han-xin XIAO
DOI: https://doi.org/10.3969/j.issn.0253-6099.2016.03.019
2016-01-01
Abstract:With analytic pure ZnO and Fe2 O3 as raw materials, zinc ferrite was prepared by using the technique of pretreatment followed by roasting process. The influences of milling time, ball size proportion, proportion of raw materials, roasting temperature and time on the preparation were investigated. It is found that with the following process conditions, including reactant mole ratio at 1∶1, loading 6 balls (Φ16.8 mm, 25.55 g/each), 3 balls (Φ8.15 mm, 3.97 g/each), 4 balls (Φ7.95 mm, 3.665 g/each), rotating speed at 200 r/min, pretreatment process for 0.5 h, roasting at 720 ℃ for 1 h, the zinc ferrite product with high purity and high crystallinity can be prepared.