Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Preparation of Zinc Oxide Nanofibers by Electrospinning

Preparation of ZnO Nanofibers with High Specific Surface Area

Preparation of ZnS Nanofibers Via Electrospinning

Oriented Nanofibers by a Newly Modified Electrospinning Method

LaMnO3 and La0.875Sr0.125MnO3 Nanofibers via Electrospinning

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Nanofibers of LiMn2O4 by electrospinning

Preparation and Characterization of Sc2o3-Doped Zro2 Nanofiber

Electrospun fibers of poly (vinyl alcohol): zinc acetate (PVA:AcZn) and further ZnO production: evaluation of PVA:AcZn ratio and annealing temperature effects on ZnO structure

LaMnO_3 and La_(0.875)Sr_(0.125)MnO_3 Nanofibers via Electrospinning

Fabrication of Mn2O3 nanowire with ultra fine morphology via an electrospinning technology

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Nanostructured LiCoO2 and LiMn2O4 fibers fabricated by a high frequency electrospinning

Preparation of Eu, Li co-doped ZnO red fluorescence nanofibers by electrospinning and their characterization

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Electrospun Zinc Oxide Nanofibers with Room-Temperature Ferromagnetism

Preparation of Li6Zr2O7 Nanofibers with High Li‐Ion Conductivity by Electrospinning

Preparation of Batio3 Nanofibers Via Electrospinning

Electrospun zirconia nanofibers and corresponding formation mechanism study

Preparation and Properties of Poly (vinyl Alcohol) Nanofibers by Electrospinning