Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Preparation of ZnO Nanofibers with High Specific Surface Area

Preparation of Zinc Oxide Nanofibers by Electrospinning

Preparation of ZnS Nanofibers Via Electrospinning

Oriented Nanofibers by a Newly Modified Electrospinning Method

Electrospun fibers of poly (vinyl alcohol): zinc acetate (PVA:AcZn) and further ZnO production: evaluation of PVA:AcZn ratio and annealing temperature effects on ZnO structure

Nanofiber template-induced preparation of ZnO nanocrystal and its application in photocatalysis

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Preparation, characterization, and the antimicrobial activity of PVA-PVP/ZnO nanofiber films via indigenous electrospinning setup

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Preparation of Eu, Li co-doped ZnO red fluorescence nanofibers by electrospinning and their characterization

PVA Nanofibers Embedded with Different Concentration of ZnO Prepared by Electrospinning Method

Preparation and Crystalline Properties of PET/ZnO Nano-meter Composite

Study on preparation process and enhanced piezoelectric performance of pine-needle-like ZnO@PVDF composite nanofibers

Photocatalytic zinc oxide on flexible polyacrylonitrile nanofibers via sol–gel coaxial electrospinning

Electrospinning preparation of Co_(0.5)Ni_(0.5)Fe_2O_4 nanofibers and its influencing factors

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Synthesis of Zn Nanofibres Through Simple Thermal Vapour-Phase Deposition

Preparation and Performance of a Novel ZnO/TM/PET Composite Negative Ion Functional Fiber

Exploration of single-crystal like electrospun Pb(Zr_(0.52)Ti_(0.48))O_3 nanofibers synthesis via electrospinning

Preparation and Properties of Zinc Oxide Films by Spin-Coating Water Solution Precursor

Growth of Nanofibers Zinc Oxide on Porous Silicon Substrates using Electrospinning Method: Effect of Temperatures