Mcraly Coating Modified By Rare Earth For High-End Equipment Parts

Jia Jin,Liu Saiyue,Meng Junsheng,Wang You

DOI: https://doi.org/10.11933/j.issn.1007-9289.20180822003

2018-01-01

China surface engineering

Abstract:Over the years, the series of MCrAlY coatings widely used in the field of high temperature protection have received continuous attention from researchers and engineers in various countries. The recent research results on the application of rare earth modification technology to the preparation of thermal sprayed MCrAlY series coatings by the Harbin Institute of Technology were summarized. The results show that the hardness of the NiCrAlY coating modified by rare earth increases by 30%-40% and the bonding strength between the coating and substrate reaches over 60 MPa. Adding rare earth can increase the thermal shock resistance of the NiCrAlY coating with the thermal shock cycles more than 100 times at 1000.. Under 1000., the NiCrAlY coating added with rare earth is still intact after 190 h, and the surface has no special change. The weight gain rate of the coatings containing 0.1% rare earth oxide is 60.53% lower than that without rare earth addition during oxidation at 1000. for 250 h. The addition of rare earth can significantly improve the high temperature vulcanization resistance and corrosion resistance of NiCrAlY coating. Rare earth modification can effectively improve the high temperature performance of the MCrAlY series coatings and meet the national requirements for high temperature protective coatings for high-end equipment components.