Abstract:This work aims to explore a method of improving the high-temperature oxidation resistance and thermal corrosion resistance of a hollow blade of gas turbine. The yttrium-modified aluminide coating was prepared on the surface of nickel-based superalloy K444 by chemical vapor deposition (CVD). The microstructure, high temperature oxidation resistance, and thermal corrosion resistance of the modified aluminide coating deposited at 950 °C, 1000 °C, and 1050 °C were compared. The microstructure and morphology of the coatings were observed and analyzed by XRD, SEM, and EDS. The results showed that adding yttrium and changing the deposition temperature had no effect on the double-layer structure (outer layer and diffusion layer) of the coating. Compared with adding yttrium, the deposition temperature had a greater effect on the coating thickness. When the deposition temperature was 1050 °C and the deposition time was 2 h, the thickness of the yttrium-modified aluminide coating increased by 33% compared to that of a single aluminide coating. The high temperature oxidation resistance and thermal corrosion resistance of the three groups of yttrium-modified aluminide coatings are better than that of the single aluminide coating. The resistance to high temperature oxidation and hot corrosion of the yttrium-modified aluminide coating deposited at 1050 °C was better than that of yttrium-modified aluminide coating deposited at 1000 °C, and both were better than that of the modified coating deposited at 950 °C. The higher the deposition temperature, the higher the yttrium content of the coating, the faster the film-forming speed of α-Al2O3, and the better the high temperature oxidation resistance and thermal corrosion resistance of the coating.

Superior oxidation resistant MCrAlY bond coats prepared by controlled atmosphere heat treatment

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Effect of Pre-Heat-Treatment on the Oxidation Resistance of MCrAlY Coatings: A Review

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Large-grain α-Al2O3 enabling ultra-high oxidation-resistant MCrAlY bond coats by surface pre-agglomeration treatment

EFFECT OF MCrAlY COATINGS ON OXIDATION RESISTANCE OF TiAl INTERMETALLICS

Advanced MCrAlY alloys with doubled TBC lifetime

Structural evolution and enhanced thermal cycling life of HVAF-sprayed NiCrAlY bond coat modified by YSZ

Study on High Temperature Properties of Yttrium-Modified Aluminide Coating on K444 Alloy by Chemical Vapor Deposition

Oxide Dispersion Strengthened Bond Coats with Higher Alumina Content: Oxidation Resistance and Influence on Thermal Barrier Coating Lifetime

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

Test atmospheres affecting voids distribution on MCrAlY-bond coats for TBCs at 1050 °C

Enhancing the Oxidation Resistance of NiCrAlY Bond Coat by High-Current Pulsed Electron Beam Irradiation

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy

Study on Microstructure and Oxidation Resistance Mechanism of Y-modified NiCrAlY Coating Prepared by Pack Cementation

Preparation of MCrAlY–Al2O3 Composite Coatings with Enhanced Oxidation Resistance through a Novel Powder Manufacturing Process

Transient oxidation behavior of MCrAlY coating irradiated by high-current pulsed electron beam

Surface Microstructure and High Temperature Oxidation Resistance of Thermal Sprayed NiCoCrAlY Bond-Coat Modified by Cathode Plasma Electrolysis

Hf and Ta co-doping MCrAlY alloy to improve the lifetime of coatings