Abstract:Microstructural modifications of a thermally sprayed MCrAlY bond coat subjected to high-current pulsed electron beam (HCPEB) and their relationships with thermal cycling behavior of thermal barrier coatings (TBCs) were investigated. Microstructural observations revealed that the rough surface of air plasma spraying (APS) samples was significantly remelted and replaced by many interconnected bulged nodules after HCPEB irradiation. Meanwhile, the parallel columnar grains with growth direction perpendicular to the coating surface were observed inside these bulged nodules. Substantial Y-rich Al2O3 bubbles and varieties of nanocrystallines were distributed evenly on the top of the modified layer. A physical model was proposed to describe the evaporation-condensation mechanism taking place at the irradiated surface for generating such surface morphologies. The results of thermal cycling test showed that HCPEB-TBCs presented higher thermal cycling resistance, the spalling area of which after 200 cycles accounted for only 1% of its total area, while it was about 34% for APS-TBCs. The resulting failure mode, i.e., in particular, a mixed delamination crack path, was shown and discussed. The irradiated effects including compact remelted surface, abundant nanoparticles, refined columnar grains, Y-rich alumina bubbles, and deformation structures contributed to the formation of a stable, continuous, slow-growing, and uniform thermally grown oxide with strong adherent ability. It appeared to be responsible for releasing stress and changing the cracking paths, and ultimately greatly improving the thermal cycling behavior of HCPEB-TBCs.

Transient oxidation behavior of MCrAlY coating irradiated by high-current pulsed electron beam

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Microstructural evolution of thermally grown oxide of an arc ion plated M CrAl X coatings after high-current pulsed electron beam treatment

Thermal Cycling Behavior of Thermal Barrier Coatings with MCrAlY Bond Coat Irradiated by High-Current Pulsed Electron Beam

Microstructural modifications and high-temperature oxidation resistance of arc ion plated NiCoCrAlYSiHf coating via high-current pulsed electron beam

Characterisation and Oxidation Behaviour of Plasma Surface Alloyed on Γ-Tial Alloy

Enhancing the Oxidation Resistance of NiCrAlY Bond Coat by High-Current Pulsed Electron Beam Irradiation

Effect of Chemical Compositions and Surface Morphologies of Mcraly Coating on Its Isothermal Oxidation Behavior

Highly Oxidation Resistant and Cost Effective MCrAlY Bond Coats Prepared by Controlled Atmosphere Heat Treatment

Effect of Microstructure on Early Oxidation of MCrAlY Coatings

Air Plasma Spraying of MCrAlY Coatings with Low Oxide Content Enabled by Adding a Deoxidizer

Surface Microstructure and High Temperature Oxidation Resistance of Thermal Sprayed NiCoCrAlY Bond-Coat Modified by Cathode Plasma Electrolysis

Mechanical, Tribological, and Oxidation Resistance Properties of NiCrAlY Coating by Atmospheric Plasma Spraying

Structural Design and High Temperature Oxidation Behavior of MCrAlY Bond Coating in the Thermal Barrier Coating System

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Microstructure features of cold-sprayed NiCoCrAlTaY coating and its high temperature oxidation behavior

Isothermal Oxidation Behavior of Nicocraltay Coating Deposited by High Velocity Air-Fuel Spraying

Development and High-Temperature Corrosion Performance of MCrAl(Y) Coatings Prepared by Electrochemical Deposition: A Brief Review

A study on the thermal cyclic behavior of NiCrAlY coatings via femtosecond laser remelting with high repetition rate

Size effects on high temperature oxidation of MCrAlY coatings processed via APS and HVOF depositions