Abstract:The severe oxidation of metal elements leads to a large amount of oxide inclusions that hinder the formation of metallurgical bonds across intersplat interfaces during thermal spraying in an ambient atmosphere, which further degrades the performance of thermally sprayed metal coatings. Controlling the oxidation of metal elements during spray deposition remains a significant challenge. In this paper, the thermodynamic and kinetic requirements of in-situ in-flight deoxidation by adding deoxidizer elements (diamond particles) to Fe / Al spray powders to achieve oxide-free molten droplets in an ambient atmosphere were investigated. Fe / Al / 2.5C composite powders containing 2.5wt.% diamond particles were prepared by mechanical alloying. Atmospheric plasma spraying (APS) was used to generate an oxide-free molten spray of FeAl particles at temperatures higher than 2 000 degrees C. This was achieved by the in-situ self-oxide cleaning effect of in-flight particles by carbon, which prevented metal droplets from oxidizing in an open atmosphere. For comparison, a FeAl coating was also deposited using Fe / Al composite powders prepared by mechanical alloying. The particle velocity and temperature were measured by a commercial thermal-spraying particle diagnostic system. The microstructures of the coatings were characterized by scanning electron microscopy and X-ray diffraction. The chemical compositions of the coatings were measured by inductively coupled plasma spectroscopy. The adhesive strength and hardness of the plasma-sprayed FeAl-based coatings were tested. The results show that under the combined effects of plasma- jet heating and the FeAl exothermic reaction, the heated FeAl spray particles could reach a high temperature of over 2 100 degrees C, which meets the thermodynamic conditions for carbon in-situ deoxidation. Because oxidation occurs from the surface of an in-flight molten droplet, to maintain continuous deoxidation of the molten FeAl droplet, the rapid transfer of carbon from the interior of the molten droplet to the surface is necessary. It was confirmed that the strong convection flow of the molten metal droplets satisfied the kinetic conditions of carbon in-situ in-flight deoxidation. The oxygen content in the APS-sprayed FeAl coatings increased with the increase of the spray distance. In contrast, the oxygen content in the APS-sprayed FeAl / 2.5C coatings decreased from 1.01 wt.% to 0.48 wt.% as the spray distance increased from 70 mm to 150 mm. This was accompanied by the decrease in carbon content from 1.41 wt.% to 0.31 wt.%, indicating the effective protection of Fe and Al from oxidation by the carbon in the droplet. Compared with the oxygen content of 3.67 wt.% in traditional FeAl coating, the oxygen content of the FeAl / 2.5C coatings was reduced to less than 0.5 wt.%. Considering that the carbon content of the coatings decreased as the spray distance increased, the results confirm that the in-flight oxidation of Fe and Al was suppressed by the preferential sacrificial oxidation of carbon in the molten droplets. Thus, the oxide in the FeAl / 2.5C coatings was mainly attributed to post-deposition oxidation. Moreover, the FeAl droplet reached the temperature to realize the spread-fusing self-metallurgical bonding effect for FeAl splats. The coatings exhibited a dense microstructure with an apparent porosity of less than 0.5%. The adhesive bonding strength of the prepared coatings exceeded 59.2 MPa owing to metallurgical bonding. The hardness of the coatings reached 590 HV0. 3, which was approximately twice that of traditional FeAl coatings. This was attributed to the reinforcement provided by the Fe3AlCx cementite phase resulting from the residual carbon in the coating.

Air Plasma Spraying of MCrAlY Coatings with Low Oxide Content Enabled by Adding a Deoxidizer

Oxidation protection dynamics of NiAl droplet by inflight in-situ carbon deoxidation during atmospheric plasma spraying for high performance NiAl coatings

Strategy to Generate Oxide-Free Molten Metal Droplets for Fully Dense Corrosion-Resistant Coatings by Atmospheric Plasma Spraying

Isothermal Oxidation Behavior of Nicocraltay Coating Deposited by High Velocity Air-Fuel Spraying

The Influence of Diamond Addition to Ni-Al Powder on Oxidation Behavior of Ni-Al During Plasma Spraying for High Performance Oxide-Free Ni-Al Intermetallic Coating

Microstructural Characteristics and Oxidation Behavior of Low-Pressure Cold-Sprayed CoNiCrAlY Coatings

Mechanical, Tribological, and Oxidation Resistance Properties of NiCrAlY Coating by Atmospheric Plasma Spraying

Investigation on the Oxidation Behavior of the NiCrAlY Bond-Coat with Low Al Content Sprayed by High Velocity Oxygen Fuel Method

Highly Oxidation Resistant and Cost Effective MCrAlY Bond Coats Prepared by Controlled Atmosphere Heat Treatment

Effect of Chemical Compositions and Surface Morphologies of Mcraly Coating on Its Isothermal Oxidation Behavior

Microstructure features of cold-sprayed NiCoCrAlTaY coating and its high temperature oxidation behavior

Study of Oxidation Behavior of Nanostructured Nicraly Bond Coatings Deposited by Cold Spraying

Effect of Suspension Plasma Spraying Power on the Microstructure and Properties of Cr2AlC Coatings

Characterization of isothermal oxidation of air plasma sprayed NiCrAlY coatings

Cold spray for production of in-situ nanocrystalline MCrAlY coatings – Part I: Process analysis and microstructure characterization

Surface Microstructure and High Temperature Oxidation Resistance of Thermal Sprayed NiCoCrAlY Bond-Coat Modified by Cathode Plasma Electrolysis

Effect of Microstructure on Early Oxidation of MCrAlY Coatings

Mechanism of Suppressing Oxidation of FeAl Molten Droplet by Adding C to Powder and Its Effect on Microstructure and Properties of Plasma-sprayed Coating

Influence of Water Vapor on the Cyclic-Oxidation Behavior of a Low-Pressure Plasma-Sprayed NiCrAlY Coating

Effect of Sprayed Powder Particle Size on the Oxidation Behavior of MCrAlY Materials During High Velocity Oxygen-Fuel Deposition

Effect of suspension plasma spraying power on the microstructure and properties of Cr 2 AlC coatings