Effect of composition of FeCoCu pre-alloyed powders on sintering characters used for diamond tools

XIE De-long,WAN Long,SONG Dong-dong,WANG Shuai,LIN Feng,L Zhi,FANG Xiao-hu,PAN Xiao-yi,QIN Hai-qing,CHEN Chao,XIAO Le-yin

DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2016.03.012

2016-01-01

Abstract:The FeCoCu pre-alloyed powders were manufactured by co-precipitation method. The microstructure was characterized, the sintering experiments were carried out, the mechanical properties and wear loss were tested and the combination condition between diamond and the powders was analyzed. The results show that the mesophases, such as Co3Fe7, CoFe15.7 and FeCu4, are formulated in the three powders, and all the powders have irregular shapes, interconnected fine particles and large surface areas. Although the solid solutions are formed, the sintering, mechanical properties and mass loss of the three powders are based on the Fe-Cu ratios. With Fe content increasing, the ideal sintering temperatures, hardness and three point bend strength raise. The relative density decreases, the wear loss becomes better. Fe-Cu ratio has important influence on the powders microstructure. The mechanical retention is the main strength in the matrix and graphitization has occurred in the diamond surface after sintering with the FeCoCu pre-alloyed powders.