Abstract:Copper based Cu–RE alloys (where RE represents lanthanum, neodymium, or samarium) with alloying content up to 16 wt-% were prepared by chill block melt spinning into ribbons of thickness between 40 and 100 μm. The melt spun ribbons were heat treated isochronally for 2 h at 300, 400, 500, 600, 700, and 800°C, respectively. The melt spun and heat treated ribbons were tested for microhardness and resistivity and were characterised by optical and transmission electron microscopy (TEM) and X-ray diffractometry (XRD). Microstructures were of the typical zone B type for Cu–1RE and Cu–3RE ribbons and of the zone B/zone A type for Cu–5RE, Cu–8RE, and Cu–12RE ribbons. Only microstructures of the zone A type were found in Cu–15La ribbons. The metastable extended solid solubilities of the rare earth elements were evaluated by measurements of the lattice parameters of the supersaturated solid solutions and significant extension from the equilibrium solid solubility was found for all three alloys. The secondary phase was identified by TEM and XRD as Cu6RE for all ribbons except Cu–15La ribbons in which metastable Cu5La and Cu13La phases were also found. Observations using TEM and XRD also showed a reduction in the α-Cu grain size of the as spun ribbons with increasing alloying content, producing nanosized α-Cu grains on the chill side of the ribbons. Heat treatment of the ribbons at 400°C for 2 h produced no significant coarsening of α-Cu grains as the size of these grains was still in the nanometer region. Both α-Cu and Cu6RE grains coarsened as a result of heat treatment for 2 h at temperatures of 600°C and above for all the alloys.

Effects of Rare Earth Additions on Compound Structure and As-Annealed Properties of Cu-12%Ag

Effects of rare-earth additions on the microstructure and strength of Cu–Ag composites

Effects of rare earth elements on annealing characteristics of Cu–6wt.% Fe composites

Effects of Cr and Zr additions on the microstructure and properties of Cu-6wt.% Ag alloys

Effects of Alloying Elements on Microstructure, Mechanical and Electrical Properties of Cu-Ag Based Alloys

Microstructure and properties of Cu–Ag, Cu–Ag–Cr and Cu–Ag–Cr–RE alloys

Effects of Rare Earth Additions on Microstructure and Properties of Cu-6%Fe Filamentary Composites

Effect of annealing processes on microstructure, mechanical properties and conductivity of Cu-12%Ag alloy composite-reinforced by fibers

Effects of pre-annealing process on microstructure and properties of the Cu-12%Ag composite wire

Microstructure evolution and properties of Cu–Ag microcomposites with different Ag content

Crystal Structure and Morphology of a Rare-Earth Compound in Cu–12 Wt.% Ag

Effects of Rare Earth Additions on Structures and Properties of Rapidly Solidified Copper Alloys

Effects of Rare Earth Additions on the Microstructural Evolution and Microhardness of Sn30Bi0.5Cu and Sn35Bi1Ag Solder Alloys

Effect of rare earth on microstructure and solderability of Sn-0.7Cu-0.075Al lead-free solder

The Effect of Rare Earths Additions on the Microstructure and the Corrosion Behavior of Sn-0.7Cu-0.075Al Solder Alloy.

Effect of Rare Earth Addition on Microstructural, Mechanical and Electrical Characteristics of Cu-6%Fe Microcomposites

Relationships between mechanical strength and electrical conductivity for Cu–Ag filamentary microcomposites

Alloying Behavior of Rare-Earth Er in Al-Cu-Mg-Ag Alloy

Effects of RE on Microstructures and Properties of Al-20Si-2Cu-1Ni Aluminum Alloy

Rare earth microalloying in as-cast and homogenized alloys Cu–6wt.% Ag and Cu–24wt.% Ag

Annealing effects on the microstructure, strength, and electrical resistivity in a dual-phase Cu-15 wt%Ag alloy