Abstract:New Cu-based bulk glassy alloys were formed in Cu–Zr–Ti and Cu–Hf–Ti systems by the copper mold casting method. The critical diameter is 4 mm for the Cu60Zr30Ti10 and Cu60Hf25Ti15 alloys which are larger than 1 mm for the Cu60Zr40 and Cu60Hf40 glassy alloys. The substitution of Zr or Hf for Ti causes an increase in the glass-forming ability (GFA). As the Ti content increases, the glass transition temperature (Tg), crystallization temperature (Tx), and the supercooled liquid region ΔTx(=Tx−Tg) decrease for both Cu60Zr40−xTix and Cu60Hf40−xTix alloys. In contrast, the liquid temperature (Tl) has a minimum value of 1127 K for the Cu60Zr20Ti20 alloy and 1175 K for the Cu60Hf20Ti20 alloy, resulting in a maximum Tg/Tl of 0.63 and 0.62, respectively. The alloys with the highest Tg/Tl value showed the highest GFA for these Cu-based alloys. The bulk glassy alloys exhibit high tensile fracture strength of 2000–2160 MPa, compressive fracture strength of 2060–2150 MPa and compressive plastic elongations of 0.8–1.7%. The finding of the new Cu-based bulk glassy alloys with high GFA, high fracture strength above 2000 MPa and distinct plastic elongation is encouraging for the future development of a new type of bulk glassy alloy which can be used for structural materials.

Fabrication of Cu-based Bulk Metallic Glasses by Binary Deep Eutectic Method

Glass forming ability, thermodynamics and mechanical properties of novel Ti–Cu–Ni–Zr–Hf bulk metallic glasses

Formation, Thermal Stability and Mechanical Properties of Ti42.5Zr7.5Cu40Ni5Sn5 Bulk Metallic Glass

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Design Of Cu8zr5-Based Bulk Metallic Glasses

Bulk Metallic Glass Formation in the Binary Cu–Zr System

Bulk metallic glass formation in the (Ti,Zr)-(Ni,Cu)-S system

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Glass-forming Ability and Thermal Stability of a New Bulk Metallic Glass in the Quaternary Zr–Cu–Ni–Al System

Composition design and mechanical properties of ternary Cu–Zr–Ti bulk metallic glasses

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Formation and Thermal Properties of Ti-Based Bulk Amorphous Alloy

Preparation and Crystallization of Ti53Cu27Ni12Zr3Al7Si3B1 Bulk Metallic Glass with Wide Supercooled Liquid Region

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

A New Centimeter‐Sized Ti‐Based Quaternary Bulk Metallic Glass with Good Mechanical Properties

Preparation of (ti0.45cu0.378zr0.10ni0.072)100−xsnx Bulk Metallic Glasses

Glass Forming Ability and Mechanical Properties of New Ni-Based Bulk Metallic Glasses

Influence of the Melting Temperature on the Fabrication of A Ti-Cu-Zr-Ni-Sn Bulk Metallic Glass

Formation and mechanical properties of Cu_(58)Zr_(20)Ti_(20)Mo_2 bulk metallic glass

Bulk Metallic Glass Formation Near the TiCu–TiNi Pseudo-Binary Eutectic Composition