Cryogenic treatment of GCr15 steel ball valve

Chengjie Liu,Jun Tan,Peng Liu,Yi Chen,Wei Li

DOI: https://doi.org/10.13251/j.issn.0254-6051.2016.06.025

2016-01-01

Abstract:Microstructure and mechanical properties of GCr 15 steel ball valve which cryogenically treated by different liquid nitrogen holding time and different temperature rising rate were studied .The results show that cryogenic treatment can induce retained austenite to transform into martensite , refine the microstructure , precipitate fine carbides and improve the comprehensive mechanical properties of GCr 15 steel ball valve.After cryogenic treatment, the retained austenite content of the steel reduced from 16.74%to 0.40%-9.75%, surface residual stress changed from -98 MPa compressive stress to 252 MPa tensile stress , wear resistance increased by 105%-146% and hardness increased by 1.70%-4.43%.When liquid nitrogen soaking time is less than 4 h, the wear rate was decreased with the soaking time extended , meanwhile, the impact absorption energy and hardness were increased .When soaking time is more than 4 h, the impact absorption energy was decreased with the extension of soaking time , while the wear rate and the hardness changed little .In addition, the hardness and wear rate were increased and impact absorption energy was decreased with the increase of temperature rising rate after liquid nitrogen soaking .The GCr15 ball valve with about 10%retained austenite after the cryogenic treatment of about 4 h liquid nitrogen soaking and about 0.5 ℃/min temperature rising rate has excellent comprehensive mechanical properties.