CHROME AND FLUORINE-FREE PRETREATMENT OF MAGNESIUM ALLOYS FOR DIRECT ELECTROLESS NICKEL PLATING

孙硕,刘建国,张伟,严川伟,王福会

DOI: https://doi.org/10.3969/j.issn.1002-6495.2009.03.018

2009-01-01

Abstract:A phosphorizing process was proposed as the pretreatment of magnesium alloy for nickel electroless plating to replace the traditional pretreatment with bathes containing chrome and fluorine.The subsequent nickel plating deposited on the phosphorized magnesium alloy was then characterized by observation of surface morphology,examination of adhesion and corrosion resistance.The pretreatment can clearly reduce the corrosion of magnesium substrate during Ni-P plating process.The potentiodynamic polarization tests indicated that the corrosion current density of Ni-P plating on AZ91 pretreated by phosphorizing process decreased by almost one order of magnitude compared to those pretreated by traditional bathes containing chrome and fluorine.After a proper heat treatment the adhesion strength of the Ni-P plating on the phosphorized substrate can reach above 23 MPa.More importantly,the new technique does not use Cr6+ and HF in its pretreatment,therefore is a much environmentally friendly process.