Microstructure and properties of Mg-9Gd-4Y-1Zn-0.5Zr alloy
MENG Bo-bo,LI Quan-an,CHEN Xiao-ya,YAN Jing-long,ZHOU Yao
DOI: https://doi.org/10.13289/j.issn.1009-6264.2017-0097
2017-01-01
Abstract:Microstructure and mechanical properties of Mg-9Gd-4Y-1Zn-0.5Zr alloy after different heat treatments were studied by means of XRD,OM,SEM,EDS analysis and tensile testing machine.The results show that in the state of casting,solid solution and aging,the microstructure of the alloy is mainly composed of α-Mg matrix and Mg5 (Gd,Y,Zn),Mg24 (Y,Gd,Zn)5,Mg12 Zn (Gd,Y) rare earth compounds.The second phase of the as-cast alloy is mainly Mg5 (Gd,Y,Zn) phase,which is parallel streamline-like with coarsegrain.After solution and aging treatment,Mg12Zn(Gd,Y) phase precipitates at grain boundaries and grows into the crystal,which is the main strengthening phase of the alloy,and the strengthening methods are mainly solid solution strengthening and aging strengthening.At room temperature,the tensile strength of the as-cast alloy is 138 MPa with the elongation of 2.16％,and the tensile strength of the aged alloy is 223 MPa,exhibiting the elongation of 3.94％.The mechanical properties of the alloy are improved obviously.