Abstract:The corrosion behavior of functionally graded cemented carbide (FGCC), with CoNiCrFe binder (WC-CoNiCrFe), has been investigated by performing electrochemical measurements and chemical characterization. The results showed that the CoNiCrFe binder was selectively dissolved in alkaline and acidic solutions. In the NaOH solution, the high contents of Ni and Co generated a passive film consisting of Co(OH) 2 , Ni(OH) 2 , Co 3 O 4 , and NiO that effectively isolated the corrosive medium from the materials. However, the contents of Fe and Cr were too low to provide satisfactory protection. In the HCl solution, the Cr element generated Cr 0 , Cr 2 O 3 , and Cr(OH) 3 . However, the Cr content was too low to form a passive film. In addition, Co, Ni and Fe in the binder were selectively dissolved in the acidic solution. Moreover, compared with the FGCC, the non-graded cemented carbide (CC) had a higher binder content and a more dispersed WC distribution. Thus, it formed a denser and thicker passive film, which was beneficial for the corrosion resistance in the NaOH solution. However, the CoNiCrFe binder was severely corroded in the HCl solution, which was due to the absence of a passive film. In comparison, the FGCC with a lower binder content and a denser WC distribution, showed a higher corrosion resistance. On the other hand, the WC grain size showed the opposite effect in alkaline and acidic solutions. In the NaOH solution, a small WC grain size increased the number of WC/CoNiCrFe interfaces, which favored the formation of a dense passive film. It, thereby reduced the probability for pitting corrosion. In the HCl solution, the corrosion generally started from grain boundaries with high interface energy as no passive film existed. Thus, a large WC grain size facilitated the improvement of the corrosion resistance. The results from the present study do not only provide a theoretical guidance for an understanding of the anticorrosion mechanism of WC-CoNiCrFe, but also a new approach for the preparation of cemented carbides with high corrosion resistance.

Electrochemical Corrosion Behaviors and Corrosion Mechanism of WC-Co Cemented Carbide in Different Aggressive Mediums

Microstructure and Corrosion Behaviour of WC-Co Coating Fabricated by Plasma Arc Welding

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Comparative Study of Corrosion Behaviors of WC-NiMo and WC-Co Cemented Carbides

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

Corrosion behavior of functionally graded cemented carbides with CoNiCrFe binder

Electrochemical corrosion behavior of hot-pressing sintered WC-Al2O3 composite in alkaline and acidic solutions

Corrosion Resistance Enhancement of WC Cermet Coating by Carbides Alloying

Preparation of Cemented Carbide and Study of Copper-Accelerated Salt Spray Corrosion and Erosion Behavior

The optimization of mechanical property and corrosion resistance of WC-6Co cemented carbide by Mo2C content

XPS and AES surface analysis of WC‐Co‐(Cr) cemented carbide after immersion in neutral solution

The corrosion performance for ultrafine WC-12Co processed by heat treatments in different pH solution

Comparison on the immersion corrosion and electrochemical corrosion resistance of WC–Al 2 O 3 composites and WC–Co cemented carbide in NaCl solution

Corrosion Behavior of Plasma Transferred Arc Fe-based Coating Reinforced by Spherical Tungsten Carbide in Hydrochloric Acid Solutions

Corrosion Behavior and Mechanism of WC-12Co Coating in Salt Spray Environment

Preparation of Chromium Carbide-Strengthened Ni-W Coatings by Electrodeposition and the Corresponding Anticorrosion Behavior in CO2-Saturated NaCl Solution

Electrochemical corrosion behavior variation of WC-10Co4Cr coating subjected to different magnetic treatments and its mechanism

Corrosion Properties and Tribological Behavior of Tungsten Carbide Coatings with Alumide Matrix of SS AISI304

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

Improving Wear Resistance and Corrosive Resistance of Cemented Carbide for Mud Pulser Rotor by Deep Cryogenic Treatment

Tribocorrosion behavior of HVOF sprayed WC-based cermet coatings in sodium chloride solution environment in relation to binder phases