Research on Microstructure and Mechanical Properties of FeCoNiAlCux High Entropy Alloys with Multi-principal Element

Shihai LIAN,Wenyi PENG,Aisheng ZHANG

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.12.001

2017-01-01

Abstract:The effects of Cu content on the microstructure and mechanical properties of FeCoNiAlCux high entropy alloys were investigated by X-ray diffraction, scanning electron microscopy with energy disperse spectroscopy, microhardness and compressive tests. The results show that FeCoNiAlCux alloys are composed of fcc phase and bcc phase. However, with the increase of Cu content, the fcc phase increases, while the bcc phase decreases. The alloys are typical dendrite microstructure. There are distinct Cu-enrichment in the interdendritic, and the increase of Cu content increases the segregation of Cu in the interdendritic, which have no change in the dendrite. Meanwhile, the increase of Cu content improves the plasticity of the alloys. FeCoNiAlCu1.5 alloy exhibits the maximum compressive strain of 36.1％. However, the yield strength and microhardness of the alloys decrease. FeCoNiAlCu0.5 alloy exhibits the maximum microhardness of 569 HV and the FeCoNiAlCu0.8 alloy exhibits the maximum yield strength of 1256 MPa.