Microstructure, Hardness, Wear Resistance, and Corrosion Resistance of As-Cast and Laser-Deposited FeCoNiCrAl0.8Cu0.5Si0.5 High Entropy Alloy

Xiaohu Ji,Lihua Zhou,Heng Li

DOI: https://doi.org/10.3390/coatings14060663

IF: 3.236

2024-05-24

Coatings

Abstract:FeCoNiCrAl0.8Cu0.5Si0.5 high-entropy alloys were fabricated using vacuum induction melting and laser deposition processes, followed by a comparison of the structural and mechanical properties of two distinct sample types. The as-cast FeCoNiCrAl0.8Cu0.5Si0.5 alloy is comprised of BCC1, BCC2, and Cr3Si phases, while the laser-deposited alloy primarily features BCC1 and BCC2 phases. Microstructural analysis revealed that the as-cast alloy exhibits a dendritic morphology with secondary dendritic arms and densely packed grains, and the laser-deposited alloy displays a dendritic structure without the formation of granular interdendritic regions. For mechanical properties, the as-cast FeCoNiCrAl0.8Cu0.5Si0.5 alloy demonstrated higher hardness than the as-deposited alloy, with values of 586 HV0.2 and 557 HV0.2, respectively. The wear rate for the as-cast alloy was observed at 3.5 × 10−7 mm3/Nm, with abrasive wear being the primary wear mechanism. Conversely, the as-deposited alloy had a wear rate of 9.0 × 10−7 mm3/Nm, characterized by adhesive wear. The cast alloy exhibited an icorr of 4.062 μA·cm−2, with pitting as the form of corrosion. The laser-deposited alloy showed an icorr of 3.621 μA·cm−2, with both pitting and intergranular corrosion observed. The laser-deposited alloy demonstrated improved corrosion resistance. The investigation of their microstructure and mechanical properties demonstrates the application potential of FeCoNiCrAl0.8Cu0.5Si0.5 alloys in scenarios requiring high hardness and enhanced wear resistance.

materials science, multidisciplinary,physics, applied, coatings & films