Study on Electroplating Time of Pulse Electroplating Ni-Cr-Mo Alloy Coating

Haipeng LIU,Zhitong ZHANG,Xinyue WANG,Qingbo MENG,Yungang LI,Haili YANG
DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.18.039
2017-01-01
Abstract:Ni-Cr-Mo alloy coatings were prepared on the surface of Q235 steel by pulse electroplating method. The effects of electroplating time on surface morphology, forming process, thickness, element content and corrosion resistance of the coating were investigated by scanning electron microscopy (SEM), glow discharge spectroscopy (GDS), Tafel curve and electrochemical impedance spectroscopy (EIS). The results show that the coating forms from the particles structure nucleating, growing and stacking from each layer. In the form of the coating, an incubation period exists. The coating is hard to become thickness for a certain time after incubation period. After this, with the electroplating time increasing, the coating is easy to become thick. With electroplating time increasing, Ni content in the coating increases, Cr content decreases and Mo content decreases. In 3. 5% NaCl solution, the corrosion resistance of the coatings strengthens firstly and then weakens. The coating prepared by electroplating for 50 min has the biggest self corrosion potential (-0. 355 V), the smallest corrosion current density (0. 006 μA·cm-2) and the biggest charge transfer resistance (26544 Ω·cm2), which exhibits the best corrosion resistance.
What problem does this paper attempt to address?