Abstract:The structural differences at various positions in the GH3625 alloy before and after magnesium treatment were statistically analyzed. In situ observation experiments were conducted at different cooling rates to examine the changes in solidification structure following magnesium treatment. A new theoretical explanation for the differential effects of magnesium treatment was proposed based on classical homogeneous nucleation theory. In practical applications, intermetallic compounds like Laves phase and metal carbides adversely affect the performance of nickel‐based superalloys. Using a high‐temperature confocal laser scanning microscope, the solidification process of as‐cast GH3625 alloy containing Mg at different cooling rates (−20, −35, and −50 °C min−1) is studied. Fitting curves of the volume fraction of the solid phase with solidification temperature before and after Mg treatment are obtained. Trends of solid phase transformation rates with solidification temperature are determined. Differential scanning calorimetry is employed to analyze and statistically evaluate the melting temperature range and enthalpy of each phase during the melting process. Experimental results demonstrate that Mg treatment significantly accelerates the alloy solidification at the cooling rates of −20 and −35 °C min−1, while reducing the area of residual liquid phase at the same solidification temperature, disrupting the Laves/NbC eutectic relationship, and regularizing NbC morphology, transitioning its distribution from aggregation to dispersion. After Mg treatment, the precipitation of the Laves phase is significantly reduced. As a result, the influence mechanism of Mg treatment on the phase transformation and microstructure of GH3625 is clarified based on homogeneous nucleation theory.

Refinement of semi-solid microstructure of self-inoculated ZA94 magnesium alloy by melt temperature

Grain Refinement Effect of Cooling Channel on ZA92 Magnesium Alloy Prepared by Self-inoculation Method

Effects of Heating Temperatures on Microstructure of Semi-solid AZ91D Magnesium Alloy During Partial Remelting

Effects of Heating Temperature on Partial Remelting Microstructure of AZ91D Magnesium Alloy

Isothermal Semisolid Microstructure Evolution of Compressively Deformed AZ91D Magnesium Alloy Billet

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Effect of Heating Process on Microstructure of AZ91D Magnesium Alloy During Partial Remelting

Microstructure evolution of semi-solid Mg e 10 Gd e 3 Y e 0 . 5 Zr alloy during isothermal heat treatment

Semi-solid Microstructure Evolution of AZ91D Magnesium Extruded by Equal Channel Angular Die

Effect of inoculant parameters on AM60 Mg alloy semisolid slurry prepared by self-inoculation method (Ⅱ)

Research on Semi-Solid Isothermal Treatment of AM60 Magnesium Alloy Processed by Severe Plastic Deformation

Microstructure evolution of semi-solid Mg–10Gd–3Y–0.5Zr alloy during isothermal heat treatment

Microstructure evolution of hot pressed AZ91D alloy chips reheated to semi-solid state

Effect of Pouring Temperature on AM60 Mg Alloy Semi-Solid Slurry Prepared by Self-Inoculation Method (I)

In Situ Observation of Microstructure and Precipitate Phase Transformation during the Solidification of Mg‐Containing GH3625 Alloy at Different Cooling Rates

Investigation of The Effect of Semi-Solid Temperatures and Holding Times at Isothermal Range On Microstructure of AZ31 Mg Alloy

Microstructure Evolution During Reheating of Extruded Mg-Gd-Y-Zr Alloy into Semisolid State

Reheating Microstructure of Refined AZ91D Magnesium Alloy in Semi-Solid State

Influences of Melt Treatment on Grain Sizes and Morphologies of Az91d Alloy

Microstructure Evolution During Remelting of High Solid Fraction ZL101 Alloy

Microstructures of Semi-Solid AZ91D Magnesium Alloys Billets Prepared by Cold Rolling SIMA Method