Abstract:The microstucture, mechanical properties and fracture behaviors of semi-continuous cast Mg-8Gd-3Y-0.5Zr (wt.%, GW83K) alloy after different heat treatments were investigated. Almost all the eutectic compounds were dissolved into the matrix and there was no evident grain growth after optimum solution treatment at 500 degrees C for 4 h. Further ageing at low temperatures led to significant precipitation hardening, which strengthened the alloy. Peak-aged at 200 degrees C, the alloy had the highest ultimate tensile strength (UTS) and lowest elongation at 395 MPa and 2.8%, respectively. When aged at 225 degrees C for 15 h, the alloy exhibited prominent mechanical performance with UTS and elongation of 363 MPa and 5.8 %, respectively. With regard to microstructure and tensile properties, the processes of 500 degrees C, 4 h + 225 degrees C, 15 h are selected as the optimal heat treatment conditions. The alloy under different conditions shows different fracture behaviors: in the as-cast alloy, a quasi-cleavage pattern is observed; after solution treatment, the alloy exhibits a trans-granular quasi-cleavage fracture; after being peak-aged at 200 degrees C and 225 degrees C, the fracture mode is a mixed mode of trans-granular and intergranular fracture, in which the inter-granular mode is dominant in the alloy peak-aged at 200 degrees C.

Microstructure evolution of semi-solid Mg e 10 Gd e 3 Y e 0 . 5 Zr alloy during isothermal heat treatment

Microstructure evolution of semi-solid Mg–10Gd–3Y–0.5Zr alloy during isothermal heat treatment

Microstructural evolution of Mg-6Zn-1.5Gd-0.4Zr alloy during semi-solid isothermal heat treatment

The Influence of Holding Time on the Microstructure Evolution of Mg–10Zn–6.8Gd–4Y Alloy During Semi-Solid Isothermal Heat Treatment

Effects of heat treatments on microstructure and mechanical properties of Mg-15Gd-5Y-0.5Zr alloy

Microstructure Evolution During Reheating of Extruded Mg-Gd-Y-Zr Alloy into Semisolid State

Study on the Influences of Different Process Temperatures on Microstructural Evolution of Mg-11%Al-2%Zn-1%Si Alloy Through Isothermal Semi-Solid Treatment

Effects of Holding Temperature and Time on Semi-Solid Isothermal Heat-Treated Microstructure of ZA84 Magnesium Alloy

Microstructural Evolution of ZA84 Magnesium Alloy During Semi-solid Isothermal Heat Treatment

Microstructure evolution and performance of Mg-8Gd-3Y-1Nd-0.5Zr alloy during heat treatment

Influence of Heat Treatment on Microstructure and Mechanical Properties of Mg-10gd-3y-1.2zn-0.4zr Alloy

Microstructure Evolution of Semi-Solid Mg-14Al-0.5Mn Alloys During Isothermal Heat Treatment

Microstructure evolution of Mg-10Gd-3Y-1.2Zn-0.4Zr alloy during heat-treatment at 773 K

Effects of Holding Temperature and Time on Semisolid Isothermal Heat Treated Microstructure of AZ61–0·7Si Magnesium Alloy

Microstructure Evolution of As-Cast AZ91 Magnesium Alloy During Isothermal Heat Treatment

Effect of Heat Treatment on Microstructure and Mechanical Properties of Mg-11Gd-2Y-5Sm-0.5Zr Alloy

Behavior of Mg–15Gd–5Y–0.5Zr alloy during solution heat treatment from 500 to 540°C

Influence of Heat Treatment on the Evolution of Microstructure and Mechanical Properties of Mg-7Gd-5Y-0.6Zn-0.8Zr Magnesium Alloy

Effects of Heating Treatment and Hot Extrusion on Microstructures and Room Temperature Mechanical Properties of Mg-10Gd-4.8Y-0.6Zr Alloy

Effects of Heat Treatment on Microstructure and Mechanical Properties of Mg-8Gd-3Y-0.5Zr (wt.%) Alloy Fabricated by Semi-Continuous Casting

Effects of Heat Treatment on Microstructure and Mechanical Properties of Mg–2·6Sm–1·3Gd–0·6Zn–0·5Zr Alloy