Microstructure evolution and performance of Mg-8Gd-3Y-1Nd-0.5Zr alloy during heat treatment
FENG Yan,LI Xiao-geng,WANG Ri-chu,PENG Chao-qun
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2017.09.05
2017-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The effects of heat treatments on the microstructures and properties of the Mg-8Gd-3Y-1Nd-0.5Zr alloy were studied. The cast Mg-8Gd-3Y-1Nd-0.5Zr alloy consists α-Mg, Mg(Gd,Y) second phases and eutectic phases of Zr-rich particle phase and β-Mg24Y5 reticular. After solid solution treatment at 520 ℃ for 24 h, the microstructure evolution of the alloy follows this sequence, α-Mg+β-Mg24Y5 phase + Mg(Gd,Y)→oversaturated α-Mg solid solution +Mg(Gd,Y) phase. After aged at 225 ℃, the second phases in the Mg-8Gd-3Y-1Nd-0.5Zr alloy precipitate following this sequence, Mg(S.S.S.S)→β″(DO19)→β′(CBCO)→β1(FCC)→β(FCC). The peak aging state occurs when the alloy is aged at 225 ℃for 24 h. The room temperature tensile strength gets 231 MPa and the elongation rate gets 3.4%, respectively. Moreover, aging treatment improves the corrosion resistance of the alloy. After aged at 225 ℃ for 72 h, stable β(FCC) phase precipitates in the Mg-8Gd-3Y-1Nd-0.5Zr alloy, which express the best corrosion resistance. The lowest average hydrogen precipitation rate is 0.22 mL/(cm2·h).