Abstract:Thermoelectric materials have a wide range of application because they can be directly used in refrigeration and power generation. And the Bi2Te3 stand out because of its excellent thermoelectric performance and are used in commercial thermoelectric devices. However, n-type Bi2Te3 has seriously hindered the development of Bi2Te3-based thermoelectric devices due to its weak mechanical properties and inferior thermoelectric performance. Therefore, it is urgent to develop a high-performance n-type Bi2Te3 polycrystalline. In this work, we employed interstitial Cu and the hot deformation process to optimize the thermoelectric properties of Bi2Te2.7Se0.3, and a high-performance thermoelectric module was fabricated based on this material. Our combined theoretical and experimental effort indicates that the interstitial Cu reduce the defect density in the matrix and suppresses the donor-like effect, leading to a lattice plainification effect in the material. In addition, the two-step hot deformation process significantly improves the preferred orientation of the material and boosts the mobility. As a result, a maximum ZT of 1.27 at 373 K and a remarkable high ZTave of 1.22 across the temperature range of 300−425 K are obtained. The TEG (7-pair) and TEC (127-pair) modules were fabricated with our n-type textured Cu0.01Bi2Te2.7Se0.3 coupled with commercial p-type Bi2Te3. The TEC module demonstrates superior cooling efficiency compared to the commercial Bi2Te3 device, achieving a ΔT of 65 and 83.4 K when the hot end temperature at 300 and 350 K, respectively. In addition, the TEG module attains an impressive conversion efficiency of 6.5% at a ΔT of 225 K, which is almost the highest value among the reported Bi2Te3-based TEG modules.

Analysis of the generating ability of the thermoelectric conversion device

Measurement and Analysis for Performance of Micro-thermoelectric Generator

Data Fitting and Analysis of Performance for Micro-thermoelectric Generator

BiSbTe alloy with high thermoelectric and mechanical performance for power generation

Design and Simulation of a Novel Thermoelectric Micro-Device with Electrodeposited Bi-Te Alloys

Thermodynamic Analysis of Thermoelectric Process and Measurement for Seebeck Coefficient of Thermoelectric Material

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi 2 Te 2.3 Se 0.7 Alloys

High Efficiency Bi2te3-Based Materials and Devices for Thermoelectric Power Generation Between 100 and 300 Degrees C

Simplified calculation model for the effect of nonlinear temperature dependence of thermoelectric properties on the conversion efficiency

High efficiency Bi2Te3-based materials and devices for thermoelectric power generation between 100 and 300 °C

Realizing a Superior Conversion Efficiency of ≈11.3% in the Group IV-VI Thermoelectric Module

Realizing High-Efficiency Thermoelectric Module by Suppressing Donor-Like Effect and Improving Preferred Orientation in N-Type Bi2(Te, Se)3

Fabrication And Evaluation Of Microscale Thermoelectric Modules Of Bi2te3-Based Alloys

Enhanced Thermoelectric Performance in N-Type Bi2Te3-Based Alloys Via Suppressing Intrinsic Excitation.

An in-depth study of nonlinear parametric characterization for thermoelectric generator modules

Bi2Te3-Based Thermoelectric Modules for Efficient and Reliable Low-Grade Heat Recovery

Design of Bi2Te3-based thermoelectric generator in a widely applicable system

Achieving High Thermoelectric Performance Through Constructing Coherent Interfaces and Building Interface Potential Barriers in N-Type Bi2Te3/Bi2Te2.7Se0.3 Nanocomposites

Performance of Bi–Te–Sb–Se Thermoelectric Material at Low Temperature

High-performance Lead-Free Cubic GeTe-based Thermoelectric Alloy

Fabrication and evaluation of microscale thermoelectric modules of Bi<sub>2</sub>Te<sub>3</sub>-based alloys