Abstract:Traditionally, preparing p-type (Bi,Sb)(2)Te-3 based materials by the combination of ball milling and hot pressing is regarded effective to reduce the lattice thermal conductivity and obtain high zT value. However, the deteriorated electrical transport properties and poor reproducibility restrict the further promotion of such technology. In this work, we prepare Bi0.4Sb1.6Te3 materials with Te self-compensation method, which leads to a high average zT value of 1.39 from 30 to 200 degrees C with significantly enhanced reproducibility. The Te self-compensation is found to be effective in manipulating the Bi(Sb)(Te)(-) and V-Te(2+) native defects in Bi0.4Sb1.6Te3 and thus suppress the "donor-like" effect caused by ball milling. The resulting enhanced carrier concentration further brings about a convergence of multi-valley bands, which leads to an increase in the density of states (DOS) near Fermi level and delays the onset of bipolar effect, in favor of improving electrical properties meanwhile reducing the bipolar thermal conductivity. Moreover, in the melting process, the excess Te facilitates the formation of Te-rich precipitates which remain in the ball-milled powders and then volatilize during the spark plasma sintering (SPS) process, thus leaving dispersedly distributed submicron pores and concequently reduced the lattice thermal conductivity. Taken together, the peak zT value reaches 1.55 at 100 degrees C and shows excellent reproducibility in three repeated measurements, which can promote the widespread application of the ball-milled (Bi,Sb)(2)Te-3 based materials in solid-state refrigeration.

Comprehensive Insight into p -Type Bi 2 Te 3 -Based Thermoelectrics near Room Temperature

High-Performance p-Type Bi 2 Te 3 -Based Thermoelectric Materials Enabled via Regulating Bi-Te Ratio

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi 2 Te 2.3 Se 0.7 Alloys

Thermoelectric performance of tellurium-reduced quaternary p -type lead–chalcogenide composites

BiSbTe alloy with high thermoelectric and mechanical performance for power generation

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi2Te2.3Se0.7 Alloys

High‐Performance Industrial‐Grade p‐Type (Bi,Sb)2Te3 Thermoelectric Enabled by a Stepwise Optimization Strategy

Enhanced Thermoelectric Properties Obtained by Compositional Optimization in P -Type Bi X Sb 2− X Te 3 Fabricated by Mechanical Alloying and Spark Plasma Sintering

The Thermoelectric Properties of Bismuth Telluride

Unraveling electronic origins for boosting thermoelectric performance of p-type (Bi,Sb) 2 Te 3

Tunable Electrical Conductivity and Simultaneously Enhanced Thermoelectric and Mechanical Properties in n-type Bi<sub>2</sub>Te<sub>3</sub>

Outstanding Room-Temperature Thermoelectric Performance of N-Type Mg3Bi2-Based Compounds Through Synergistically Combined Band Engineering Approaches

Enhanced Thermoelectric Performance in N-Type Bi2Te3-Based Alloys Via Suppressing Intrinsic Excitation.

High Efficiency Bi2te3-Based Materials and Devices for Thermoelectric Power Generation Between 100 and 300 Degrees C

Thermoelectric Performance Enhancement in N -Type Bi 2 (tese) 3 Alloys Owing to Nanoscale Inhomogeneity Combined with a Spark Plasma-Textured Microstructure

Synergistic Texturing and Bi/Sb‐Te Antisite Doping Secure High Thermoelectric Performance in Bi 0.5 Sb 1.5 Te 3 ‐Based Thin Films

Comprehensive Investigation on the Thermoelectric Properties of P‐type PbTe‐PbSe‐PbS Alloys

Substituted (P, As, Sb, S and Se) of two dimensional Bi2Te3 monolayer under stress at high temperature: achieving high thermoelectric performance

High efficiency Bi2Te3-based materials and devices for thermoelectric power generation between 100 and 300 °C

Critical Role of Tellurium Self-Compensation in Enhancing the Thermoelectric Performance of P-Type Bi0.4Sb1.6Te3 Alloy

High Thermoelectric Performance Bismuth Telluride Prepared by Cold Pressing and Annealing Facilitating Large Scale Application