Abstract:Grain refinement strongly strengthens the non‐basal slip of Bi2Te3‐based thermoelectric material, and then increase the carrier concentration, hindering the practical preparation of n‐type Bi2Te3 by ball milling method. In this work, enhancing the ball milling energy can facilitate the recovery effect during hot pressing, which can reduce and stabilize the carrier concentration and achieve high thermoelectric and mechanical performances. The carrier concentration in n‐type layered Bi2Te3‐based thermoelectric (TE) material is significantly impacted by the donor‐like effect, which would be further intensified by the nonbasal slip during grain refinement of crushing, milling, and deformation, inducing a big challenge to improve its TE performance and mechanical property simultaneously. In this work, high‐energy refinement and hot‐pressing are used to stabilize the carrier concentration due to the facilitated recovery of cation and anion vacancies. Based on this, combined with SbI3 doping and hot deformation, the optimized carrier concentration and high texture degree are simultaneously realized. As a result, a peak figure of merit (zT) of 1.14 at 323 K for Bi2Te2.7Se0.3 + 0.05 wt.% SbI3 sample with the high bending strength of 100 Mpa is obtained. Furthermore, a 31‐couple thermoelectric cooling device consisted of n‐type Bi2Te2.7Se0.3 + 0.05 wt.% SbI3 and commercial p‐type Bi0.5Sb1.5Te3 legs is fabricated, which generates the large maximum temperature difference (ΔTmax) of 85 K at a hot‐side temperature of 343 K. Thus, the discovery of recovery effect in high energy refinement and hot‐pressing has significant implications for improving TE performance and mechanical strength of n‐type Bi2Te3, thereby promoting its applications in harsh conditions.

Thermoelectric Performance Enhancement in N -Type Bi 2 (tese) 3 Alloys Owing to Nanoscale Inhomogeneity Combined with a Spark Plasma-Textured Microstructure

Multi-scale hierarchical microstructure modulation towards high room temperature thermoelectric performance in <i>n</i>-type Bi<sub>2</sub>Te<sub>3</sub>-based alloys

Tunable Electrical Conductivity and Simultaneously Enhanced Thermoelectric and Mechanical Properties in n‐type Bi2Te3

Tunable Electrical Conductivity and Simultaneously Enhanced Thermoelectric and Mechanical Properties in n-type Bi<sub>2</sub>Te<sub>3</sub>

Development of Nanostructured Bi2Te3 with High Thermoelectric Performance by Scalable Synthesis and Microstructure Manipulations

Isotropic Thermoelectric Performance of Layer-Structured n-Type Bi 2 Te 2.7 Se 0.3 by Cu Doping

Fine-Tuning Bi2Te3-Copper Selenide Alloys Enables an Efficient n-Type Thermoelectric Conversion

Achieving High Thermoelectric Performance of n-Type Bi 2 Te 2.79 Se 0.21 Sintered Materials by Hot-Stacked Deformation

Enhanced Thermoelectric and Mechanical Properties of p-type Bi0.5Sb1.5Te3 Bulk Alloys by Composite Electroless Plating with Ni&Cu

Synergistical Enhancement of Thermoelectric Properties in N‐type Bi2O2Se by Carrier Engineering and Hierarchical Microstructure

Enhanced Thermoelectric Performance of N-Type Bi2Te2.7Se0.3 Via a Simple Liquid-Assisted Shear Exfoliation

Enhancing Thermoelectric Performance of N-Type Hot Deformed Bismuth-Telluride-Based Solid Solutions by Nonstoichiometry-Mediated Intrinsic Point Defects.

High-performance near-room-temperature n-type Bi2Te3-based thermoelectric alloys with superior mechanical properties

Synergistic Texturing and Bi/Sb‐Te Antisite Doping Secure High Thermoelectric Performance in Bi 0.5 Sb 1.5 Te 3 ‐Based Thin Films

Enhanced Thermoelectric Properties Obtained by Compositional Optimization in P -Type Bi X Sb 2− X Te 3 Fabricated by Mechanical Alloying and Spark Plasma Sintering

Broad-Temperature Thermoelectric Figure of Merit Enhancement in Unconventional n-Type Bi 2 Te 2.3 Se 0.7 Alloys

Modulation of Vacancy Defects and Texture for High Performance N-Type Bi2 Te3 Via High Energy Refinement.

Modulation of Vacancy Defects and Texture for High Performance n‐Type Bi2Te3 via High Energy Refinement

High-Performance p-Type Bi 2 Te 3 -Based Thermoelectric Materials Enabled via Regulating Bi-Te Ratio

High‐Performance Industrial‐Grade p‐Type (Bi,Sb)2Te3 Thermoelectric Enabled by a Stepwise Optimization Strategy

Enhancing Thermoelectric Performance of n-Type Bi2Te2.7Se0.3 through Incorporation of Amorphous Si3N4 Nanoparticles